PC AC3610 BK FCFC TAIWAN
TAIRILITE®
Automotive sector
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | FCFC TAIWAN/AC3610 BK |
|---|---|---|---|
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 122 |
| R 级, 23°C | ASTM D785 | 122 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC3610 BK |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 99.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2150 Mpa |
| tensile strength | 23°C | ASTM D638 | 67.0 Mpa |
| flammability | Test Condition | Test Method | FCFC TAIWAN/AC3610 BK |
|---|---|---|---|
| UL flame retardant rating | 1.0 mm | UL 94 | V-0 |
| 2.0 mm | UL 94 | 5VB | |
| 1.2 mm | UL 94 | V-0 | |
| 1.5 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC3610 BK |
|---|---|---|---|
| Shrinkage rate | 流动 : 3.20 mm | ASTM D955 | 0.50 - 0.70 % |
| 3.20 mm | ISO 2577 | 0.50 - 0.70 % | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC3610 BK |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 3.18 mm，HDT | ASTM D648 | 113 °C |
| injection | Test Condition | Test Method | FCFC TAIWAN/AC3610 BK |
|---|---|---|---|
| drying time | 4.0 to 6.0 hr | ||
| Injection Pressure | 4.90 to 12.7 Mpa | ||
| Processing (melt) temperature | 260 to 295 °C | ||
| drying temperature | 110 to 120 °C | ||
| Temperature | 80 to 100 °C |