Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BKV25FN01 900116 LANXESS GERMANY
Durethan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/BKV25FN01 900116 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/BKV25FN01 900116 |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA6.GFHR.10-090.GF25 |
| Electrical performance | Test Condition | Test Method | LANXESS GERMANY/BKV25FN01 900116 |
|---|---|---|---|
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 39 KV/mm |
| Volume resistivity | 23°C | IEC 60093 | 5E+15 ohms·cm |
| Surface Resistivity | IEC 60093 | 4E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/BKV25FN01 900116 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178/A | 9200 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.8 % |
| Bending Strain | 23°C | ISO 178/A | 3.3 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 130 Mpa |
| bending strength | 3.5%Strain,23°C | ISO 178/A | -- Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 9500 Mpa |
| bending strength | 23°C4 | ISO 178/A | 210 Mpa |
| flammability | Test Condition | Test Method | LANXESS GERMANY/BKV25FN01 900116 |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 775 °C |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | LANXESS GERMANY/BKV25FN01 900116 |
|---|---|---|---|
| Shrinkage rate | MD:120°C,4小时,2.00mm3 | ISO 2577 | 0.10 % |
| MD:260°C,2.00mm2 | ISO 2577 | 0.30 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.5 % |
| 饱和,23°C | ISO 62 | 5.0 % | |
| Shrinkage rate | TD:260°C,2.00mm2 | ISO 2577 | 0.60 % |
| TD:120°C,4小时,2.00mm3 | ISO 2577 | 0.10 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/BKV25FN01 900116 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 222 °C | |
| vicat | ISO 306/B120 | 213 °C | |
| ball-indentation hardness | 210°C | IEC 60695-10-2 | Pass |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 202 °C |
Contact Us
Get App
Top