PBT 420SE0 SABIC INNOVATIVE US
VALOX™
Lawn equipment、Garden equipment、Industrial applications、Automotive External Parts、Electrical field、Electronic field、Architectural application、Outdoor applications、Electrical appliances、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Automotive interior parts、Casters、Household goods、Petroleum Applications、Natural gas supplies、sporting goods、Textile application、Lighting applications
Glass fiber reinforced、dimensional stability 、High rigidity、high strength、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/420SE0 |
---|---|---|---|
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 45 kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 45 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ASTM D256 | 57 J/m |
23°C | ASTM D256 | 60 J/m | |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 5.00 J |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 6.0 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
23°C | ASTM D4812 | 620 J/m | |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.0 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 50 kJ/m² |
hardness | Test Condition | Test Method | SABIC INNOVATIVE US/420SE0 |
---|---|---|---|
Rockwell hardness | R级 | ISO 2039-2 | 119 |
ball-indentation hardness | H358/30 | ISO 2039-1 | 118 Mpa |
Rockwell hardness | R级 | ASTM D785 | 119 |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/420SE0 |
---|---|---|---|
Tensile modulus | ISO 527-2/1 | 10000 Mpa | |
tensile strength | 断裂 | ISO 527-2/5 | 120 Mpa |
elongation | 屈服 | ASTM D638 | 2.0 % |
Tensile strain | 屈服 | ISO 527-2/5 | 1.9 % |
bending strength | Break,50.0mmSpan | ASTM D790 | 186 Mpa |
Flexural modulus | 50.0mmSpan | ASTM D790 | 9800 Mpa |
tensile strength | 屈服 | ISO 527-2/5 | 120 Mpa |
Tensile modulus | ASTM D638 | 12000 Mpa | |
elongation | 断裂 | ASTM D638 | 2.0 % |
tensile strength | Break | ASTM D638 | 120 Mpa |
bending strength | ISO 178 | 180 Mpa | |
Flexural modulus | ISO 178 | 9500 Mpa | |
Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 22.0 mg |
Tensile strain | 断裂 | ISO 527-2/5 | 1.9 % |
tensile strength | 屈服 | ASTM D638 | 120 Mpa |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/420SE0 |
---|---|---|---|
relative permittivity | 60Hz | IEC 60250 | 3.30 |
Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
relative permittivity | 100Hz | IEC 60250 | 3.80 |
dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 16 KV/mm |
relative permittivity | 1MHz | IEC 60250 | 3.30 |
Compared to the Leakage Tracking Index (CTI) | -- | IEC 60112 | PLC 3 |
Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
60Hz | IEC 60250 | 1E-03 | |
High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 22 KV/mm |
arc resistance | ASTM D495 | PLC6 | |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 23 KV/mm |
relative permittivity | 50Hz | IEC 60250 | 3.30 |
Dissipation Factor | 1MHz | ASTM D150 | 0.020 |
High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
Dissipation Factor | 100Hz | IEC 60250 | 2E-03 |
dielectric constant | 1MHz | ASTM D150 | 3.70 |
100Hz | ASTM D150 | 3.80 | |
Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | PLC 4 |
Dissipation Factor | 1MHz | IEC 60250 | 0.010 |
Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
dielectric strength | 3.20mm,inAir | ASTM D149 | 19 KV/mm |
Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
dielectric strength | 1.60mm,在油中 | ASTM D149 | 24 KV/mm |
flammability | Test Condition | Test Method | SABIC INNOVATIVE US/420SE0 |
---|---|---|---|
UL flame retardant rating | 2.0mm | UL 94 | 5VA |
Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
Limiting Oxygen Index | ISO 4589-2 | 32 % | |
UL flame retardant rating | 0.40mm | UL 94 | V-2 |
0.71mm | UL 94 | V-0 |
physical property | Test Condition | Test Method | SABIC INNOVATIVE US/420SE0 |
---|---|---|---|
Shrinkage rate | MD:3.20mm | 内部方法 | 0.50-0.70 % |
TD:--2 | 内部方法 | 0.40-0.80 % | |
Outdoor applicability | UL 746C | f2 | |
Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 29.0 cm3/10min |
Shrinkage rate | TD:3.20mm | 内部方法 | 0.50-1.0 % |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.070 % |
Shrinkage rate | MD:--2 | 内部方法 | 0.10-0.50 % |
Water absorption rate | 饱和,23°C | ISO 62 | 0.090 % |
density | ASTM D792 | 1.63 g/cm³ | |
Specific volume | ASTM D792 | 0.610 cm³/g | |
density | ISO 1183 | 1.63 g/cm³ | |
melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 42 g/10min |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/420SE0 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,Unannealed,100mmSpan,HDT | ISO 75-2/Be | 220 °C |
Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 2.5E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 212 °C |
vicat | ASTM D152511 | 200 °C | |
Heat distortion temperature | 1.8MPa,未退火,100mm跨距9,HDT | ISO 75-2/Ae | 195 °C |
RTI Str | UL 746 | 140 °C | |
Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距10,HDT | ISO 75-2/Af | 200 °C |
vicat | -- | ISO 306/B120 | 200 °C |
thermal conductivity | ISO 8302 | 0.25 W/m/K | |
Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 8.9E-05 cm/cm/°C |
MD:-40to40°C | ISO 11359-2 | 2.5E-05 cm/cm/°C | |
vicat | -- | ISO 306/A50 | 220 °C |
-- | ISO 306/B50 | 200 °C | |
Linear coefficient of thermal expansion | TD:-40to40°C | ISO 11359-2 | 8.9E-05 cm/cm/°C |
MD:23到80°C | ISO 11359-2 | 2.5E-05 cm/cm/°C | |
RTI Imp | UL 746 | 130 °C | |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 200 °C |
Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
RTI Elec | UL 746 | 130 °C |