Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HIPS SRG100 HK PETROCHEMICAL
--
Toy、Office supplies
heat-resisting、High impact resistance、High gloss
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | HK PETROCHEMICAL/SRG100 |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 72 |
| Mechanical properties | Test Condition | Test Method | HK PETROCHEMICAL/SRG100 |
|---|---|---|---|
| Tensile modulus | 3.20mm | ASTM D638 | 2000 Mpa |
| elongation | 断裂,3.20mm | ASTM D638 | 58 % |
| tensile strength | 屈服,3.20mm | ASTM D638 | 30.0 Mpa |
| Flexural modulus | 3.20mm | ASTM D790 | 2100 Mpa |
| bending strength | 3.20mm | ASTM D790 | 52.0 Mpa |
| tensile strength | 3.20mm | ASTM D638 | 23.0 Mpa |
| optical performance | Test Condition | Test Method | HK PETROCHEMICAL/SRG100 |
|---|---|---|---|
| gloss | 60° | ASTM D523 | 98 |
| flammability | Test Condition | Test Method | HK PETROCHEMICAL/SRG100 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | HK PETROCHEMICAL/SRG100 |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 3.5 g/10min |
| Apparent density | ASTM D1895 | 0.65 g/cm³ |
| Thermal performance | Test Condition | Test Method | HK PETROCHEMICAL/SRG100 |
|---|---|---|---|
| vicat | -- | ASTM D15255 | 96.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,12.7mm，HDT | ASTM D648 | 90.0 °C |
| vicat | -- | ASTM D15254 | 103 °C |