Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DL-003 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical Applications,Automotive components,Engine parts
High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DL-003 |
|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火,3.20mm | ASTM D648 | 128 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 131 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DL-003 |
|---|---|---|---|
| Bending modulus | ASTM D790 | 2190 Mpa | |
| ISO 178 | 2400 Mpa | ||
| bending strength | ISO 178 | 84.1 Mpa | |
| ASTM D790 | 80.3 Mpa | ||
| elongation | 断裂 | ASTM D638 | 38 % |
| 屈服 | ASTM D638 | 6.1 % | |
| Friction coefficient | Dynamic | ASTM D3702Modified | 0.18 |
| Static | ASTM D3702Modified | 0.070 | |
| Tensile modulus | ASTM D638 | 2070 Mpa | |
| ISO 527-2/1 | 2200 Mpa | ||
| Tensile strain | 屈服 | ISO 527-2 | 5.5 % |
| tensile strength | 屈服 | ASTM D638 | 51.7 Mpa |
| 屈服 | ISO 527-2 | 53.0 Mpa | |
| 断裂 | ASTM D638 | 47.6 Mpa | |
| 断裂 | ISO 527-2 | 50.0 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 60.0 10^-10in^5-min/ft-lb-hr |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DL-003 |
|---|---|---|---|
| Shrinkage rate | TD:24小时 | ISO 294-4 | 0.88 % |
| MD：24小时 | ASTM D955 | 0.80-0.90 % | |
| MD:24小时 | ISO 294-4 | 0.83 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.12 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/DL-003 |
|---|---|---|---|
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 30.6 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 29 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 34.1 J | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 140 kJ/m² |