PC EXL9132 SABIC INNOVATIVE JAPAN

LEXAN™

Electronic and Electrical Applications,Aerospace Applications

High mobility,Ductility at low temperat,Short molding cycle

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/EXL9132
Ball Pressure Test	H358/30	ISO 2039-1	95.0 Mpa

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/EXL9132
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	124 °C
		0.45MPa,Unannealed,3.20mm	ASTM D648	136 °C
		0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	136 °C
		1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	124 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.2E-05 cm/cm/°C
		TD：-40to40°C	ASTME831	7.2E-05 cm/cm/°C
		TD：23to80°C	ISO 11359-2	7.5E-05 cm/cm/°C
		MD：23to80°C	ISO 11359-2	7.5E-05 cm/cm/°C
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	50.0 °C
RTI Str		UL 746	50.0 °C
Vicat softening temperature	--	ISO 306/B120	144 °C
		--	ISO 306/B50	143 °C
			ASTM D152510	143 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/EXL9132
Bending modulus	50.0mmSpan	ASTM D790	2340 Mpa
Bending modulus			ISO 178	2300 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	95.1 Mpa
bending strength			ISO 178	88.0 Mpa
elongation	Break	ASTM D638	100 %
elongation		Yield	ASTM D638	5.8 %
Tensile modulus		ASTM D638	2270 Mpa
Tensile modulus			ISO 527-2/1	2200 Mpa
Tensile strain	Break	ISO 527-2/50	100 %
Tensile strain		Yield	ISO 527-2/50	5.0 %
tensile strength	Yield	ASTM D638	58.1 Mpa
		Yield	ISO 527-2/50	59.0 Mpa
		Break	ISO 527-2/50	55.0 Mpa
		Break	ASTM D638	58.5 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/EXL9132
Compared to the anti leakage trace index		IEC 60112	PLC 3
Dielectric strength	3.20mm,in Oil	IEC 60243-1	19 KV/mm
Dissipation factor	1MHz	IEC 60250	0.010
		50Hz	IEC 60250	4E-04
		60Hz	IEC 60250	4E-04
Relative permittivity	60Hz	IEC 60250	2.70
		50Hz	IEC 60250	2.70
		1MHz	IEC 60250	2.70

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/EXL9132
density		ISO 1183	1.19 g/cm³
density			ASTM D792	1.18 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	17 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	16.0 cm3/10min
Shrinkage rate	TD：3.20mm	Internal Method	0.40-0.80 %
Shrinkage rate		MD：3.20mm	Internal Method	0.40-0.80 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Water absorption rate		Saturation,23°C	ISO 62	0.35 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/EXL9132
Charpy Notched Impact Strength	23°C	ISO 179/1eA	60 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	25 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	67.9 J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	20 kJ/m²
		23°C	ISO 180/1A	55 kJ/m²
		23°C	ASTM D256	730 J/m
		-30°C	ASTM D256	560 J/m
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	NoBreak
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	NoBreak

flammability	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/EXL9132
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	40 %
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	825 °C
UL flame retardant rating	3.0mm	UL 94	5VA
UL flame retardant rating		1.5mm	UL 94	V-0