PPS A503X05 BK TORAY JAPAN
Torelina®
Fiber grade
High impact resistance,High temperature resistan,Flame retardant,Glass fiber reinforced,High mobility,enhance,Low temperature resistanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | TORAY JAPAN/A503X05 BK |
---|---|---|---|
Combustibility (rate) | UL 94 | V-0 | |
Hot deformation temperature | HDT | ASTM D648/ISO 75 | >260 ℃(℉) |
Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 2.6(流动)3.9(横向) mm/mm.℃ | |
Melting temperature | 278 ℃(℉) |
mechanical properties | Test Condition | Test Method | TORAY JAPAN/A503X05 BK |
---|---|---|---|
Bending modulus | ASTM D790/ISO 178 | 12 kg/cm²(MPa)[Lb/in²] | |
bending strength | ASTM D790/ISO 178 | 220 kg/cm²(MPa)[Lb/in²] | |
Charpy Notched Impact Strength | ASTM D256/ISO 179 | 25 kg·cm/cm(J/M)ft·lb/in | |
Elongation at Break | ASTM D638/ISO 527 | 1.5 % | |
Rockwell hardness | ASTM D785 | 120 | |
tensile strength | ASTM D638/ISO 527 | 140 kg/cm²(MPa)[Lb/in²] |
Electrical performance | Test Condition | Test Method | TORAY JAPAN/A503X05 BK |
---|---|---|---|
Dielectric constant | ASTM D150/IEC 60250 | 3.2 | |
Volume resistivity | ASTM D257/IEC 60093 | 1014 Ω.cm |
other | Test Condition | Test Method | TORAY JAPAN/A503X05 BK |
---|---|---|---|
characteristic | 30%加纤.增强.标准 | ||
Color | 黑 |
Physical properties | Test Condition | Test Method | TORAY JAPAN/A503X05 BK |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1.57 | |
Shrinkage rate | ASTM D955 | 0.3 % | |
Water absorption rate | ASTM D570/ISO 62 | 0.02 % |