PA6 Polimid B 40 EM2 Poliblend S.p.a.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | Poliblend S.p.a./Polimid B 40 EM2 |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2 | 2500 MPa |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 14 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 75 MPa |
| elongation at break | 23°C | ISO 527-2 | 90 % |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NB kJ/m² |
| Electrical performance | Test Condition | Test Method | Poliblend S.p.a./Polimid B 40 EM2 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | >600 V |
| Volume resistivity | IEC 60093 | 1E+14 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | Poliblend S.p.a./Polimid B 40 EM2 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 0.80mm | |
| UL -94 | HB 1.50mm | ||
| UL -94 | HB 3.00mm |
| physical property | Test Condition | Test Method | Poliblend S.p.a./Polimid B 40 EM2 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 1.6/8.5 % |
| Shrinkage rate | TD | ISO 294-4 | 1.5 % |
| MD | ISO 294-4 | 1.1 % | |
| density | ISO 1183 | 1.09 g/cm³ |
| Thermal performance | Test Condition | Test Method | Poliblend S.p.a./Polimid B 40 EM2 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 70 °C |
| vicat | 熔融温度 | ISO 11357-3 | 222 °C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 170 °C |
| Linear coefficient of thermal expansion | 耐热/球压测试 | IEC 60695-10-2 | >165 °C |
| 长期使用温度 | 80 °C | ||
| vicat | B9.8N | ISO 306/B50 | 200 °C |