Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 1330G ASAHI JAPAN
Leona™
Engine hood parts、Automotive sector、Industrial applications、component
Lubricity、Low friction coefficient、high strength
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/1330G |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 71 kJ/m² |
| hardness | Test Condition | Test Method | ASAHI JAPAN/1330G |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 89 |
| R计秤 | ISO 2039-2 | 120 | |
| M计秤 | ISO 2039-2 | 89 | |
| R计秤 | ASTM D785 | 120 |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/1330G |
|---|---|---|---|
| Water absorption rate | 湿 | 1.4 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/1330G |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 98(118) J/m |
| bending strength | ASTM D790 | 245 Mpa | |
| flexural coefficient | 干(湿) | ASTM D-790 | 8.0(6.3) GPa |
| Tensile modulus | 23°C | ISO 527-2 | 9800 Mpa |
| tensile strength | 干(湿) | ASTM D-638 | 157(118) Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 8040(MPa) kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 245(MPa) kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | 断裂,23°C | ISO 527-2 | 144 Mpa |
| Rockwell hardness | ASTM D785 | R120 | |
| Flexural modulus | ASTM D790 | 8000 Mpa | |
| tensile strength | ASTM D638 | 157 Mpa | |
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(108) R scale |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| Rockwell hardness | 干(湿) | ASTM D-785 | 89(60) M Scale |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| bending strength | 23°C | ISO 178 | 235 Mpa |
| 干(湿) | ASTM D-790 | 245(177) Mpa | |
| Flexural modulus | 23°C | ISO 178 | 8700 Mpa |
| elongation at break | 干(湿) | ASTM D-638 | 3(3) % |
| other | Test Condition | Test Method | ASAHI JAPAN/1330G |
|---|---|---|---|
| characteristic | 高刚性.润滑性 | ||
| purpose | 轴受部件 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/1330G |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.5-1.0 % | |
| density | ASTM D792/ISO 1183 | 1.48 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.4 % |
| flammability | Test Condition | Test Method | ASAHI JAPAN/1330G |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHI JAPAN/1330G |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.50 % |
| Wear factor | 湿 | ASTM D-1044 | 9 ×10-6kg/1000times |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
| Shrinkage rate | 吸水率(饱和,23°C) | 内部方法 | -- % |
| TD | 内部方法 | 1.0 % | |
| 干 | 旭化成方法 | 0.5-1.0 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/1330G |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 248 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 260 °C | |
| 1.82MPa,干，HDT | ASTM D-648 | 248 °C | |
| HDT | ASTM D648/ISO 75 | 248 ℃（℉） | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 261 °C | |
| 0.46MPa,干，HDT | ASTM D-648 | 260 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 246 °C | |
| UL flame retardant rating | 干 | UL 94 | HB |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 3E-05 cm/cm/°C |
| 干 | ASTM D-696 | 3 ×10-5/K |