Product Name / Manufacturer / Model

Reference Price

PPA DUPONT USA HTN42G30EF NC010

US$ 5,870 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	DUPONT USA/HTN42G30EF NC010
bending strength		ISO 178	210 Mpa
Tensile strain	Break	ISO 527-2	1.7 %
tensile strength	Break	ISO 527-2	134 Mpa
Tensile modulus		ISO 527-2	11700 Mpa
Bending modulus		ISO 178	11300 Mpa
thermal performance	Test Condition	Test Method	DUPONT USA/HTN42G30EF NC010
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	5.1E-5 cm/cm/°C
RTI Elec	0.40 mm	UL 746	130 °C
RTI Elec		3.0 mm	UL 746	130 °C
RTI Imp	3.0 mm	UL 746	120 °C
RTI Imp		0.40 mm	UL 746	115 °C
RTI	3.0 mm	UL 746	130 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.0E-5 cm/cm/°C
		Flow : -40 to 23°C	ISO 11359-2	1.7E-5 cm/cm/°C
		Across Flow : -40 to 23°C	ISO 11359-2	4.3E-5 cm/cm/°C
		Across Flow : 55 to 160°C	ISO 11359-2	8.4E-5 cm/cm/°C
RTI	0.40 mm	UL 746	125 °C
Linear coefficient of thermal expansion	Flow : 55 to 160°C	ISO 11359-2	2.0E-5 cm/cm/°C
Melting temperature		ISO 11357-3	314 °C
flammability	Test Condition	Test Method	DUPONT USA/HTN42G30EF NC010
Hot filament ignition temperature	0.40 mm	IEC 60695-2-13	750 °C
		3.0 mm	IEC 60695-2-13	825 °C
		1.5 mm	IEC 60695-2-13	800 °C
Burning wire flammability index	0.40 mm	IEC 60695-2-12	960 °C
UL flame retardant rating		UL 94	V-0
Burning wire flammability index	1.5 mm	IEC 60695-2-12	960 °C
Burning wire flammability index		3.0 mm	IEC 60695-2-12	960 °C
injection	Test Condition	Test Method	DUPONT USA/HTN42G30EF NC010
Mold temperature			110 to 130 °C
Processing (melt) temperature			325 to 335 °C
drying temperature			100 °C
Drying time - hot air dryer			6.0 to 8.0 hr
Mold temperature	Drying Recommended		yes
Suggested maximum moisture content			0.10 %
Physical properties	Test Condition	Test Method	DUPONT USA/HTN42G30EF NC010
Shrinkage rate	Flow	ISO 294-4	0.40 %
Shrinkage rate		横向Flow	ISO 294-4	0.90 %
Biobased carbon content		ISO 16620-2	21 %
impact performance	Test Condition	Test Method	DUPONT USA/HTN42G30EF NC010
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	35 kJ/m²
Electrical performance	Test Condition	Test Method	DUPONT USA/HTN42G30EF NC010
Compared to the anti leakage trace index		IEC 60112	PLC 0
Volume resistivity		IEC 62631-3-1	1.0E+16 ohms·m
Dielectric strength		IEC 60243-1	33 KV/mm