PC/ABS GP-5306F LG CHEM KOREA
LUPOY®
Electronic field,Electrical field,Laptop case,Electrical/Electronic Applications
Flame retardant,Glass fiber reinforced,enhance,Filler: Glass fiber reinf,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/GP-5306F |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | 2.0 % |
| tensile strength | 屈服,3.20mm | ASTM D638 | 108 Mpa |
| Flexural modulus | 3.20mm | ASTM D790 | 8140 Mpa |
| bending strength | 屈服,3.20mm | ASTM D790 | 167 Mpa |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/GP-5306F |
|---|---|---|---|
| Volume resistivity | 23°C | ASTM D257 | 1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | CTI)4 | UL 746 | PLC 3 |
| arc resistance | ASTM D495 | PLC6 | |
| dielectric strength | 23°C,1.00mm | ASTM D149 | 26 KV/mm |
| flammability | Test Condition | Test Method | LG CHEM KOREA/GP-5306F |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LG CHEM KOREA/GP-5306F |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 4.0 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.40-0.90 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.080 % |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/GP-5306F |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 185 °C |
| melting temperature | ASTM D3418 | 223 °C | |
| RTI Imp | UL 746 | 60.0 °C | |
| RTI Str | UL 746 | 60.0 °C | |
| RTI Elec | UL 746 | 60.0 °C |