Product Name
Brand Name
Usages
Properties
Certificates
PC 123R-111 SABIC EU
LEXAN™
Electronic and electrical、Automotive Applications
Low viscosity、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC EU/123R-111 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 11 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 65 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC EU/123R-111 |
|---|---|---|---|
| ball-indentation hardness | H 358/30 | ISO 2039-1 | 95.0 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC EU/123R-111 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2350 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 63.0 Mpa |
| bending strength | ISO 178 | 90.0 Mpa | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 10.0 mg |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 65.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC EU/123R-111 |
|---|---|---|---|
| relative permittivity | 50 Hz | IEC 60250 | 2.70 |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.010 |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Dissipation Factor | 60 Hz | IEC 60250 | 1.0E-3 |
| 50 Hz | IEC 60250 | 1.0E-3 | |
| relative permittivity | 1 MHz | IEC 60250 | 2.70 |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| relative permittivity | 60 Hz | IEC 60250 | 2.70 |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm |
| optical performance | Test Condition | Test Method | SABIC EU/123R-111 |
|---|---|---|---|
| transmissivity | 2540 µm | ASTM D1003 | 88.0 to 90.0 % |
| refractive index | ISO 489 | 1.586 | |
| Haze ratio | 2540 µm | ASTM D1003 | < 0.80 % |
| flammability | Test Condition | Test Method | SABIC EU/123R-111 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | HB |
| 0.75 mm | UL 94 | HB | |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 850 °C |
| Limiting Oxygen Index | ISO 4589-2 | 25 % |
| physical property | Test Condition | Test Method | SABIC EU/123R-111 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 21.0 cm3/10min |
| Outdoor applicability | UL 746C | f1 | |
| Shrinkage rate | Flow | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.35 % |
| Thermal performance | Test Condition | Test Method | SABIC EU/123R-111 |
|---|---|---|---|
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| vicat | -- | ISO 306/B120 | 141 °C |
| ball-indentation hardness | 140°C8 | IEC 60695-10-2 | 通过 |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Be | 133 °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Ae | 122 °C | |
| vicat | -- | ISO 306/B50 | 140 °C |
| RTI Imp | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | 23 到 80°C，流动 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C |
| injection | Test Condition | Test Method | SABIC EU/123R-111 |
|---|---|---|---|
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 270 to 290 °C | ||
| Temperature at the rear of the barrel | 260 to 280 °C | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Hopper temperature | 60 to 80 °C | ||
| drying temperature | 120 °C | ||
| Temperature at the front of the material cylinder | 280 to 300 °C | ||
| Temperature | 80 to 100 °C | ||
| Spray nozzle temperature | 270 to 290 °C |