PPO WCD801A-BK1066 SABIC INNOVATIVE SHANGHAI
FLEX NORYL™
Electronic and electrical
Food grade
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD801A-BK1066 |
|---|---|---|---|
| Shore hardness | 邵氏 A, 30 秒 | ASTM D2240 | 80 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD801A-BK1066 |
|---|---|---|---|
| elongation | 断裂4 | ASTM D638 | 120 % |
| 断裂 | ISO 527-2/50 | 120 % | |
| tensile strength | 断裂1 | UL 1581 | 16.0 Mpa |
| 断裂, 113°C3 | UL 1581 | 17.0 Mpa | |
| Flexural modulus | -- | ISO 178 | 90.0 Mpa |
| tensile strength | 断裂2 | ASTM D638 | 12.0 Mpa |
| elongation | 断裂1 | UL 1581 | 210 % |
| Flexural modulus | 100 mm 跨距 | ASTM D790 | 80.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 13.0 Mpa |
| elongation | 断裂, 113°C5 | UL 1581 | 150 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD801A-BK1066 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| relative permittivity | 50 Hz | IEC 60250 | 2.80 |
| Dissipation Factor | 1 MHz | IEC 60250 | 4.0E-3 |
| Volume resistivity | IEC 60093 | 3.8E+15 ohms·cm | |
| Dissipation Factor | 60 Hz | IEC 60250 | 0.030 |
| relative permittivity | 1 MHz | IEC 60250 | 2.80 |
| Dissipation Factor | 50 Hz | IEC 60250 | 0.030 |
| relative permittivity | 60 Hz | IEC 60250 | 2.80 |
| dielectric strength | 2.00 mm, 在油中 | IEC 60243-1 | 23 KV/mm |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD801A-BK1066 |
|---|---|---|---|
| Smoke density | Non-Flaming, Ds max : 500.0 µm | ASTM E662 | 95 |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 750 °C |
| Smoke density | Flaming, Ds max : 500.0 µm | ASTM E662 | 140 |
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 650 °C |
| Limiting Oxygen Index | ISO 4589-2 | 26 % | |
| UL flame retardant rating | 4.0 mm | UL 94 | V-0 |
| Limiting Oxygen Index | VW-11 | UL 1581 | Pass |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD801A-BK1066 |
|---|---|---|---|
| melt mass-flow rate | 250°C/5.0 kg | ASTM D1238 | 11 g/10 min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD801A-BK1066 |
|---|---|---|---|
| Heat distortion temperature | 100°C | UL 1581 | 16 % |
| brittle temperature | ASTM D746 | < -40.0 °C | |
| UL temperature rating | UL 1581 | 80 °C |