PPA AT-6115HS BK324 SOLVAY USA
AMODEL®
Industrial applications、Automotive Applications、Valves/valve components、Parts under the hood of a、Vehicle electronics、Application in the automo、Machine/mechanical compon、Laptop case、currency、Metal substitution、Industrial components、Shell
High temperature resistan、Thermal stability、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/AT-6115HS BK324 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 76 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/AT-6115HS BK324 |
|---|---|---|---|
| bending strength | ASTM D790 | 165 Mpa | |
| Flexural modulus | 100°C | ISO 178 | 2340 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 5200 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 126 Mpa |
| 断裂,24°C | ISO 527-2 | 68.3 Mpa | |
| Flexural modulus | ASTM D790 | 4410 Mpa | |
| Tensile modulus | 100°C | ISO 527-2 | 3100 Mpa |
| tensile strength | ASTM D638 | 122 Mpa | |
| Tensile strain | 断裂,24°C | ISO 527-2 | 7.7 % |
| bending strength | 100°C | ISO 178 | 66.9 Mpa |
| Tensile modulus | ASTM D638 | 5380 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.4 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.1 % |
| bending strength | 23°C | ISO 178 | 170 Mpa |
| Flexural modulus | 23°C | ISO 178 | 4270 Mpa |
| shear strength | ASTM D732 | 56.5 Mpa | |
| compressive strength | ASTM D695 | 100 Mpa |
| physical property | Test Condition | Test Method | SOLVAY USA/AT-6115HS BK324 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 1.0 % |
| Water absorption rate | 24hr | ASTM D570 | 0.20 % |
| Shrinkage rate | TD | ASTM D955 | 1.1 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/AT-6115HS BK324 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 305 °C | |
| Linear coefficient of thermal expansion | TD：100到200°C | ASTME831 | 1.2E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTM D648 | 260 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 298 °C | |
| Linear coefficient of thermal expansion | MD：100到200°C | ASTME831 | 3E-05 cm/cm/°C |
| TD：0to100°C | ASTME831 | 9E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 251 °C |
| melting temperature | ASTM D3418 | 305 °C | |
| Linear coefficient of thermal expansion | MD：0to100°C | ASTME831 | 2.2E-05 cm/cm/°C |