PBT 420-1001 SABIC INNOVATIVE US
VALOX™
Lawn equipment,Garden equipment,Industrial applications,Automotive External Parts,Electrical field,Electronic field,Architectural application field,Outdoor applications,Electrical appliances,Engine hood parts,Medical supplies,Nursing supplies,Plastic bag,Automotive interior parts,Casters,Household goods,Petroleum Applications,Natural gas supplies,sporting goods,Textile application,Lighting applications
Glass fiber reinforced,dimensional stability ,High rigidity,high strength,heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/420-1001 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| -30°C | ISO 179/1eA | 5.0 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 8.00 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| 23°C | ISO 180/1A | 8.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| -30°C | ISO 179/1eU | 45 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 45 kJ/m² |
| 23°C | ISO 180/1U | 45 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/420-1001 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 122 Mpa |
| Rockwell hardness | R级 | ISO 2039-2 | 118 |
| R级 | ASTM D785 | 118 |
| Supplementary Information | Test Condition | Test Method | SABIC INNOVATIVE US/420-1001 |
|---|---|---|---|
| filler | ASTM D229 | 30 % |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/420-1001 |
|---|---|---|---|
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTM D648 | 207 °C |
| 0.45MPa,未退火,6.40mm | ASTM D648 | 216 °C | |
| 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 217 °C | |
| 0.45MPa,未退火,3.20mm | ASTM D648 | 220 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 203 °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 204 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 2.5E-05 cm/cm/°C | |
| MD：-40to40°C | ASTME831 | 2.5E-05 cm/cm/°C | |
| MD：60to138°C | ASTME831 | 2.5E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 140 °C | |
| RTI Imp | UL 746 | 140 °C | |
| RTI Str | UL 746 | 140 °C | |
| thermal conductivity | ISO 8302 | 0.19 W/m/K | |
| vicat | ASTM D152514 | 215 °C | |
| -- | ISO 306/A50 | 223 °C | |
| -- | ISO 306/B120 | 215 °C | |
| -- | ISO 306/B50 | 215 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/420-1001 |
|---|---|---|---|
| bending strength | Yield,50.0mmSpan | ASTM D790 | 195 Mpa |
| ISO 178 | 195 Mpa | ||
| Break,50.0mmSpan | ASTM D790 | 190 Mpa | |
| flexural modulus | 50.0mmSpan | ASTM D790 | 7580 Mpa |
| ISO 178 | 8500 Mpa | ||
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 19.0 mg |
| Tensile modulus | ASTM D638 | 9300 Mpa | |
| ISO 527-2/1 | 9300 Mpa | ||
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| Yield | ASTM D638 | 2.7 % | |
| 屈服 | ISO 527-2/5 | 2.0 % | |
| Break | ASTM D638 | 2.7 % | |
| tensile strength | Yield | ASTM D638 | 120 Mpa |
| 断裂 | ISO 527-2/5 | 125 Mpa | |
| 屈服 | ISO 527-2/5 | 125 Mpa | |
| Break | ASTM D638 | 120 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/420-1001 |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| CTI | UL 746 | PLC 0 | |
| dielectric constant | 1MHz | ASTM D150 | 3.70 |
| 100Hz | ASTM D150 | 3.80 | |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 28 KV/mm |
| 3.20mm,在油中 | IEC 60243-1 | 16 KV/mm | |
| 1.00mm15 | IEC 60243-1 | 19 KV/mm | |
| 1.60mm,在油中 | IEC 60243-1 | 24 KV/mm | |
| 3.20mm,inAir | ASTM D149 | 19 KV/mm | |
| 1.60mm,在油中 | ASTM D149 | 25 KV/mm | |
| Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
| 1MHz | ASTM D150 | 0.020 | |
| 100Hz | IEC 60250 | 1E-03 | |
| 1MHz | IEC 60250 | 0.010 | |
| 60Hz | IEC 60250 | 1E-03 | |
| 50Hz | IEC 60250 | 1E-03 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| relative permittivity | 60Hz | IEC 60250 | 3.10 |
| 50Hz | IEC 60250 | 3.10 | |
| 1MHz | IEC 60250 | 3.10 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | ASTM D257 | >3.2E+16 ohms·cm | |
| IEC 60093 | >1.0E+15 ohms·cm |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/420-1001 |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 17 g/10min |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 13.0 cm3/10min |
| shrinkage rate | TD：3.20mm | 内部方法 | 0.50-1.0 % |
| MD：--4 | 内部方法 | 0.50-0.80 % | |
| MD：--3 | 内部方法 | 0.30-0.50 % | |
| MD：--2 | 内部方法 | 0.30-0.70 % | |
| TD：--3 | 内部方法 | 0.40-0.60 % | |
| TD：--2 | 内部方法 | 0.50-1.0 % | |
| TD：--5 | 内部方法 | 0.60-0.90 % | |
| MD：3.20mm | 内部方法 | 0.30-0.80 % | |
| Specific volume | ASTM D792 | 0.660 cm³/g | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.080 % |
| 24hr | ASTM D570 | 0.090 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/420-1001 |
|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 750 °C |
| Limiting Oxygen Index | ASTM D2863 | 19 % | |
| UL flame retardant rating | 0.8mm | UL 94 | HB |