PPO HS1000X-701 SABIC INNOVATIVE US
NORYL™
medical care
Glass fiber mineral reinf、 Mineral fiber reinforced、14%MF
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | SABIC INNOVATIVE US/HS1000X-701 |
|---|---|---|---|
| Water absorption rate | 24hrs | ASTM D-570 | 0.07 % |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HS1000X-701 |
|---|---|---|---|
| Flexural modulus | 6.4mm | ASTM D-790 | 2894 Mpa |
| tensile strength | 屈伏点，3.2mm | ASTM D-638 | 65 Mpa |
| Impact strength of cantilever beam gap | 23°C | ASTM D-256 | 133 J/m |
| tensile strength | 断裂点，3.2mm | ASTM D-638 | 30 Mpa |
| Rockwell hardness | ASTM D-785 | 121 | |
| bending strength | 6.4mm | ASTM D-790 | 103 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HS1000X-701 |
|---|---|---|---|
| Volume resistivity | ASTM D-257 | 2.0×10 Ω.cm | |
| dielectric constant | 1MHz | ASTM D-150 | 2.83 |
| Surface Resistivity | ASTM D-257 | 1.0×10 Ω.cm |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HS1000X-701 |
|---|---|---|---|
| Shrinkage rate | 3.2mm | ASTM D-955 | 5-7 |
| enhance | 14 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HS1000X-701 |
|---|---|---|---|
| Long term use temperature | 无冲击 | UL 746B | 100 °C |
| Heat distortion temperature | 1.8MPa，HDT | ASTM D-648 | 93 °C |
| 0.45MPa，HDT | ASTM D-648 | 98 °C | |
| vicat | ASTM D-1525 | 125 °C | |
| Long term use temperature | 含冲击 | UL 746B | 85 °C |
| 电气 | UL 746B | 100 °C |