Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA/MXD6 N-252-11 MITSUBISHI ENGINEERING JAPAN
RENY™
Electronic and Electrical、Automotive sector
High rigidity、High impact、Filler: Glass mineral、25% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/N-252-11
Melt Volume-Flow Rate (MVR)
275°C/2.16kg
ISO1133
cm3/10min
1
Melt mass flow rate
275°C/2.16kg
ISO1133
g/10min
2
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/N-252-11
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
3
Tensile modulus
ISO527-2
Mpa
2
tensile strength
断裂
ISO527-2
Mpa
1
elongation
断裂
ISO527-2
%
1
Bending modulus
ISO178
Mpa
2
bending strength
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/N-252-11
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
4
Electrical performance
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/N-252-11
Surface resistivity
IEC60093
ohms
4
Dielectric strength
1.00mm
IEC60243-1
KV/mm
2
Leakage Trace Index
IEC60112
V
3
Volume resistivity
IEC60093
ohms·cm
6