Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 FR50-BK153J DUPONT SHENZHEN
Zytel®
Fitness equipment,Automotive sector,Electrical field,Electronic field,Electrical appliances
Flame retardant,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | DUPONT SHENZHEN/FR50-BK153J |
|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 240 °C |
| Melting temperature | ISO 11357-3 | 262 °C |
| mechanical properties | Test Condition | Test Method | DUPONT SHENZHEN/FR50-BK153J |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.6 % |
| tensile strength | 断裂 | ISO 527-2 | 170 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT SHENZHEN/FR50-BK153J |
|---|---|---|---|
| Compared to the anti leakage trace index | IEC 60112 | PLC 2 | |
| Dielectric strength | 2.00 mm | IEC 60243-1 | 24 KV/mm |
| Surface resistivity | IEC 62631-3-2 | -- ohms | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 ohms·m |
| Physical properties | Test Condition | Test Method | DUPONT SHENZHEN/FR50-BK153J |
|---|---|---|---|
| Shrinkage rate | 横向流量 | ISO 294-4 | 0.80 % |
| 流量 | ISO 294-4 | 0.30 % | |
| Water absorption rate | 24 hr, 23°C, 2.00 mm | ISO 62 | 0.60 % |
| impact performance | Test Condition | Test Method | DUPONT SHENZHEN/FR50-BK153J |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 50 kJ/m² |
| -30°C | ISO 179/1eU | 50 kJ/m² | |
| 23°C | ISO 179/1eU | 60 kJ/m² |
| flammability | Test Condition | Test Method | DUPONT SHENZHEN/FR50-BK153J |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| injection | Test Condition | Test Method | DUPONT SHENZHEN/FR50-BK153J |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Maintain pressure | Drying Recommended | yes | |
| 50.0 to 100 Mpa | |||
| Maximum Screw Tangential Speed | 12 m/min | ||
| Melt Temperature, Optimum | 290 °C | ||
| Mold temperature | 70 to 120 °C | ||
| Mold Temperature, Optimum | 100 °C | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Suggested maximum moisture content | 0.20 % |