POM/PTFE KL-4540-NAT SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Medical and nursing suppl、Electrical appliances、Plastic bag
Low extract、Internal lubrication
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/KL-4540-NAT |
|---|---|---|---|
| 23°C | ASTM D4812 | 620 J/m | |
| Dart impact equipped with measuring instruments | 23°C, Energy at Peak | ASTM D3763 | 3.00 J |
| 23°C 6 | ISO 180/1U | 42 kJ/m² | |
| Dart impact equipped with measuring instruments | -- | ISO 6603-2 | 1.00 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KL-4540-NAT |
|---|---|---|---|
| Tensile modulus | -- 1 | ASTM D638 | 1830 Mpa |
| tensile strength | 屈服 2 | ASTM D638 | 43.0 Mpa |
| 断裂 | ISO 527-2/5 | 39.0 Mpa | |
| elongation | 屈服 2 | ASTM D638 | 14 % |
| Flexural modulus | -- 4 | ISO 178 | 2080 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 22 % |
| Bending stress | 断裂, 50.0 mm 跨距 3 | ASTM D790 | 63.0 Mpa |
| -- | ISO 178 | 60.0 Mpa | |
| Friction coefficient 5 | Dynamic | ASTM D3702 | 0.25 |
| Static | ASTM D3702 | 0.14 | |
| tensile strength | 屈服 | ISO 527-2/5 | 39.0 Mpa |
| Flexural modulus | 50.0 mm 跨距 3 | ASTM D790 | 2020 Mpa |
| Wear factor 5 | ASTM D3702 | 1.8E+6 10^-8 mm³/N·m | |
| Tensile modulus | -- | ISO 527-2/1 | 2020 Mpa |
| tensile strength | 断裂 2 | ASTM D638 | 43.0 Mpa |
| elongation | 断裂 2 | ASTM D638 | 30 % |
| 断裂 | ISO 527-2/5 | 43 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/KL-4540-NAT |
|---|---|---|---|
| Shrinkage rate | 流动 : 24小时 | ASTM D955 | 2.1 到 2.9 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.43 % |
| 24 hr, 50% RH | ASTM D570 | 0.18 % | |
| Shrinkage rate | 横向流动 : 24小时 | ASTM D955 | 2.1 到 2.9 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KL-4540-NAT |
|---|---|---|---|
| 横向 : -40 到 40°C | ASTM E831 | 1.1E-4 cm/cm/°C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 87.0 °C |
| 流动 : -40 到 40°C | ASTM E831 | 1.1E-4 cm/cm/°C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6 | ISO 75-2/Af | 79.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/KL-4540-NAT |
|---|---|---|---|
| Temperature | 80 到 110 °C | ||
| screw speed | 30 到 60 rpm | ||
| Temperature at the rear of the barrel | 175 到 190 °C | ||
| Processing (melt) temperature | 200 到 215 °C | ||
| Back pressure | 0.200 到 0.300 Mpa | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 210 到 220 °C | ||
| drying time | 4.0 hr | ||
| Temperature in the middle of the barrel | 195 到 205 °C |