ABS A3000XC SABIC INNOVATIVE US

LNP™ STAT-KON™

Electronic and electrical components,Automotive Applications

Conductive,high strength

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/A3000XC
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	88.0 °C
		0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Bf	91.0 °C
		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	76.0 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Af	76.0 °C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	1.0E-4 cm/cm/°C
		Across Flow : 23 to 60°C	ISO 11359-2	1.0E-4 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	9.3E-5 cm/cm/°C
		Flow : 23 to 60°C	ISO 11359-2	9.3E-5 cm/cm/°C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/A3000XC
Bending modulus	--5	ISO 178	1980 Mpa
Bending modulus		50.0 mm Span4	ASTM D790	2090 Mpa
bending strength	Break, 50.0 mm Span4	ASTM D790	65.0 Mpa
bending strength		--5,6	ISO 178	59.0 Mpa
elongation	Break	ISO 527-2/5	24 %
		Yield3	ASTM D638	3.1 %
		Yield	ISO 527-2/5	3.0 %
		Break3	ASTM D638	6.0 %
Tensile modulus	--2	ASTM D638	2060 Mpa
Tensile modulus		--	ISO 527-2/1	2010 Mpa
tensile strength	Break	ISO 527-2/5	31.0 Mpa
		Yield	ISO 527-2/5	38.0 Mpa
		Break3	ASTM D638	36.0 Mpa
		Yield3	ASTM D638	39.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/A3000XC
Surface resistivity		ASTM D257	1.0E+9 - 1.0E+11 ohms

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/A3000XC
Shrinkage rate	Flow : 24hr	ASTM D955	0.40 %
Shrinkage rate		Across FlowFlow : 24hr	ASTM D955	0.50 %
Water absorption rate	24 hr, 50% RH	ASTM D570	1.1 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/A3000XC
Dart impact	23°C, Energy at Peak	ASTM D3763	32.0 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂

injection	Test Condition	Test Method	SABIC INNOVATIVE US/A3000XC
Back pressure			0.200 to 0.300 Mpa
drying temperature			70 to 80 °C
drying time			4.0 hr
Mold temperature			10 to 50 °C
Processing (melt) temperature			200 to 210 °C
Screw speed			30 to 60 rpm
Suggested maximum moisture content			0.050 to 0.10 %
Temperature at the front of the material cylinder			205 to 215 °C
Temperature at the rear of the barrel			180 to 195 °C
Temperature in the middle of the barrel			195 to 205 °C