Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PTFE DL-4020EP SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™
Plastic bag、Electrical appliances、Electronic and Electrical
Easy to form、Easy to demould
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DL-4020EP |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DL-4020EP |
|---|---|---|---|
| coefficient of friction | Dynamic | ASTM D3702 | 0.28 |
| elongation | 断裂 | ASTM D638 | 53 % |
| bending strength | ASTM D790 | 81.0 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 53.0 Mpa |
| coefficient of friction | Static | ASTM D3702 | 0.17 |
| Flexural modulus | ASTM D790 | 2270 Mpa | |
| Wear factor | ASTM D3702 | 2.0E+7 10^-8 mm³/N·m |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DL-4020EP |
|---|---|---|---|
| Shrinkage rate | 流动 : 24小时 | ASTM D955 | 0.70 - 0.90 % |
| 横向流动 : 24小时 | ASTM D955 | 0.70 - 0.90 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DL-4020EP |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 128 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DL-4020EP |
|---|---|---|---|
| drying time | 4.0 hr | ||
| screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 305 to 315 °C | ||
| Temperature at the rear of the barrel | 295 to 305 °C | ||
| Processing (melt) temperature | 300 to 315 °C | ||
| drying temperature | 120 °C | ||
| Temperature at the front of the material cylinder | 310 to 320 °C | ||
| Back pressure | 0.200 to 0.300 Mpa | ||
| Temperature | 80 to 110 °C |