Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS CL DENKA JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DENKA JAPAN/CL |
|---|---|---|---|
| melt mass-flow rate | 200℃,49N | ISO 1133(JIS K7210) | 2.7 g/10min |
| density | 23℃ | ISO 1183(JIS K7112) | 1080 kg/m |
| melt mass-flow rate | 220℃,98N | ISO 1133(JIS K7210) | 34 g/10min |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/CL |
|---|---|---|---|
| Flexural modulus | 2mm/min | ISO 178(JIS K7171) | 2000 Mpa |
| Rockwell hardness | 23℃ | ISO 2039-2(JIS K7202) | 31 M |
| Charpy Notched Impact Strength | 23℃ | ISO 179(JIS K7111) | 14 KJ/m |
| bending strength | 2mm/min | ISO 178(JIS K7171) | 62 Mpa |
| Tensile stress | 50mm/min | ISO 527-1 | 42 Mpa |
| optical performance | Test Condition | Test Method | DENKA JAPAN/CL |
|---|---|---|---|
| Total Light Transmittance | 2mmt | ISO 13468-1(JIS K7361) | 91 % |
| Haze ratio | 2mmt | ISO 14782(JIS 7136) | 2.0 % |
| physical property | Test Condition | Test Method | DENKA JAPAN/CL |
|---|---|---|---|
| Shrinkage rate | DENKA Method | 0.4 % |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/CL |
|---|---|---|---|
| vicat | 50N | ISO 306(JIS K7206) | 80 °C |
| Heat distortion temperature | 1.80MPa | ISO 75-1 | 64 °C |
| combustibility | UL 94 | HB |