Melt Volume-Flow Rate (MVR)

280°C/2.16kg

ISO1133

cm3/10min

4

Shrinkage rate

TD

ISO294-4

%

0

Shrinkage rate

TD3

ISO294-4

%

1

Shrinkage rate

MD

ISO294-4

%

0

Shrinkage rate

MD3

ISO294-4

%

0

Water absorption rate

饱和,23°C,2.00mm

ISO62

%

2

Water absorption rate

平衡,23°C,2.00mm,50%RH

ISO62

%

0

Impact strength of simply supported beam without notch

-30°C

ISO179/1eU

kJ/m²

2

Impact strength of simply supported beam without notch

23°C

ISO179/1eU

kJ/m²

5

Tensile modulus

ISO527-2

Mpa

4

tensile strength

断裂

ISO527-2

Mpa

7

elongation

断裂

ISO527-2

%

5

Bending modulus

ISO178

Mpa

3

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

2

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

2

Melting temperature

ISO11357-3

°C

2

vicat softening point

ISO306/B50

°C

2

Linear coefficient of thermal expansion

MD

ISO11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

MD:-40到23°C

ISO11359-2

cm/cm/°C

9

Linear coefficient of thermal expansion

MD:55到160°C

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD:-40到-23°C

ISO11359-2

cm/cm/°C

4

Linear coefficient of thermal expansion

TD:55到160°C

ISO11359-2

cm/cm/°C

3

Linear coefficient of thermal expansion

EffectiveThermalDiffusivity

ISO11359-2

m²/s

9

Surface resistivity

IEC60093

ohms

1

Leakage Trace Index

IEC60112

V

3

Volume resistivity

IEC60093

ohms·cm

1

Extreme Oxygen Index

ISO4589-2

%

1

Burning rate

1.00mm

ISO3795

mm/min

<