PA66 G4000HSL NC01 INVISTA USA
TORZEN®
Electrical field、Electronic field、Automotive sector
Thermal stability、Glass fiber reinforced、dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | INVISTA USA/G4000HSL NC01 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 12300 Mpa | |
| Charpy Notched Impact Strength | -40℃ | ISO 179 | 10 kJ/m² |
| bending strength | ISO 178 | 320 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Flexural modulus | ISO 178 | 10300 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 225 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 13 kJ/m² |
| Impact strength of cantilever beam gap | 23℃ | ISO 180 | 13 kJ/m² |
| other | Test Condition | Test Method | INVISTA USA/G4000HSL NC01 |
|---|---|---|---|
| characteristic | 40%玻纤增强 | ||
| purpose | 汽车配件 |
| physical property | Test Condition | Test Method | INVISTA USA/G4000HSL NC01 |
|---|---|---|---|
| Shrinkage rate | MD: 2.00 mm | ISO 294-4 | 0.35-0.45 % |
| MD:2.00mm | ISO 294-4 | 0.35-0.45 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.70 % |
| Shrinkage rate | TD: 2.00 mm | ISO 294-4 | 0.85-0.95 % |
| Water absorption rate | 23℃, 24 hr | ISO 62 | 0.70 % |
| 平衡,23°C,50%RH | ISO 62 | 1.1 % | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.85-0.95 % |
| Water absorption rate | 平衡, 23℃, 50% RH | ISO 62 | 1.1 % |
| Thermal performance | Test Condition | Test Method | INVISTA USA/G4000HSL NC01 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 260 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 260 °C | |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 250 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 250 °C |