PA46 TS200F6 BG89102 DSM HOLAND

Stanyl®

Electronic and electrical components,Electrical applications

Flame retardant,heat-resisting

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	DSM HOLAND/TS200F6 BG89102
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	290 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/A	290 °C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	6.0E-5 cm/cm/°C
Linear coefficient of thermal expansion		Flow	ISO 11359-2	2.5E-5 cm/cm/°C
Melting temperature		ISO 11357-3	295 °C
RTI Elec	0.8 mm	UL 746	65.0 °C
Thermal Index - 5000 hr		IEC 60216	152 °C

mechanical properties	Test Condition	Test Method	DSM HOLAND/TS200F6 BG89102
Bending modulus	--	ISO 178	9000 Mpa
		120°C	ISO 178	4700 Mpa
		160°C	ISO 178	3900 Mpa
Tensile modulus	200°C	ISO 527-2	4000 Mpa
		--	ISO 527-2	10000 Mpa
		120°C	ISO 527-2	5500 Mpa
		160°C	ISO 527-2	5000 Mpa
		180°C	ISO 527-2	4400 Mpa
Tensile strain	Break, 180°C	ISO 527-2	7.5 %
		Break, 160°C	ISO 527-2	7.5 %
		Break, 120°C	ISO 527-2	7.5 %
		Break	ISO 527-2	4.0 %
		Break, 200°C	ISO 527-2	7.5 %
tensile strength	Break, 120°C	ISO 527-2	110 Mpa
		Break, 200°C	ISO 527-2	90.0 Mpa
		Break	ISO 527-2	210 Mpa
		Break, 180°C	ISO 527-2	95.0 Mpa
		Break, 160°C	ISO 527-2	100 Mpa

Electrical performance	Test Condition	Test Method	DSM HOLAND/TS200F6 BG89102
Compared to the anti leakage trace index		IEC 60112	V
Dielectric strength		IEC 60243-1	35 KV/mm
Relative permittivity	100 Hz	IEC 60250	4.40
Relative permittivity		1 MHz	IEC 60250	4.00
Volume resistivity		IEC 60093	1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	DSM HOLAND/TS200F6 BG89102
density		ISO 1183	1.41 g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.3 %
Shrinkage rate		Flow	ISO 294-4	0.50 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.6 %

impact performance	Test Condition	Test Method	DSM HOLAND/TS200F6 BG89102
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	11 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	11 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	12 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	65 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	80 kJ/m²

flammability	Test Condition	Test Method	DSM HOLAND/TS200F6 BG89102
Flammability level		UL 94	HB