PC Iupilon® E-2000 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® E-2000
Charpy Notched Impact Strength23°CISO 17988 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® E-2000
Nominal tensile fracture strainISO 527-2110 %
Tensile modulusISO 527-22400 MPa
Tensile strain屈服ISO 527-25.4 %
tensile strength 屈服ISO 527-260.0 MPa
Flexural modulusISO 1782300 MPa
bending strengthISO 17893.0 MPa
Electrical performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® E-2000
dielectric strength3.00mmIEC 60243-118 kV/mm
Volume resistivityIEC 600933E+16 ohms·cm
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602506E-04
dielectric strength1.00mmIEC 60243-131 kV/mm
relative permittivity1MHzIEC 602503.10
Surface ResistivityIEC 600936E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 2
Dissipation Factor1MHzIEC 602509E-03
physical property Test ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® E-2000
Shrinkage rateTD:3.20mm0.50to0.70 %
MD:3.20mm0.50to0.70 %
Water absorption rate饱和,23°CISO 620.24 %
Melt volume flow rate300°C/1.2kgISO 11335.00 cm³/10min
densityISO 11831.20 g/cm³
melt mass-flow rate300°C/1.2kgISO 11335.3 g/10min
Thermal performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® E-2000
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B145 °C
1.8MPa,未退火，HDTISO 75-2/A131 °C
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C
TDISO 11359-26.6E-05 cm/cm/°C