Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PEI AUR200G6 SABIC INNOVATIVE US
ULTEM™
Automotive Applications,Electrical applications
Thermal stability,High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/AUR200G6 |
---|---|---|---|
0.45MPa, unannealed, 100mm span | ISO 75-2/Be | 205 °C | |
1.8MPa, unannealed, 100mm span | ISO 75-2/Ae | 200 °C | |
Linear coefficient of thermal expansion | MD:23to150°C | ISO 11359-2 | 2.5E-05 cm/cm/°C |
TD:23to150°C | ISO 11359-2 | 6E-05 cm/cm/°C | |
thermal conductivity | ISO 8302 | 0.30 W/m/K |
mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/AUR200G6 |
---|---|---|---|
Bending modulus | ISO 178 | 6500 Mpa | |
bending strength | ISO 178 | 180 Mpa | |
Tensile modulus | ISO 527-2/1 | 8000 Mpa | |
Tensile strain | Break | ISO 527-2/5 | 3.0 % |
tensile strength | Break | ISO 527-2/5 | 120 Mpa |
Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/AUR200G6 |
---|---|---|---|
melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 7.5 g/10min |
Shrinkage rate | MD1 | Internal Method | 0.20-0.40 % |
Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.50 % |
Saturation,23°C | ISO 62 | 0.90 % |
impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/AUR200G6 |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.0 kJ/m² |