Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6T A335K BK MITSUI CHEM JAPAN
ARLEN™
Automotive sector
Glass fiber reinforced、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | MITSUI CHEM JAPAN/A335K BK |
|---|---|---|---|
| Melting Temperature | 320 °C | ||
| Heat Deflection Temperature | ASTM D-648 | 310 °C | |
| Flame retardancy | UL 94 | HB | |
| Glass Transition Temperature | 125 °C | ||
| Coefficient of Linear Thermal Expansion | ASTM D-696 | 2.0 |
| Physical | Test Condition | Test Method | MITSUI CHEM JAPAN/A335K BK |
|---|---|---|---|
| Modeling Shrinkage | 2mmt | ASTM D-955 | 0.3 % |
| Moisture Absorption | 23℃ | ASTM D-570 | 0.3 % |
| Mechanical Properties | Test Condition | Test Method | MITSUI CHEM JAPAN/A335K BK |
|---|---|---|---|
| Tensile Strength | dry(moist) | ASTM D-638 | 240(220) Mpa |
| Rockwell Hardness | ASTM D-785 | 110 M Scale | |
| IZOD Notch Impact Strength | dry(moist) | ASTM D-256 | 130(150) J/m |
| Flexural Modulus | dry(moist) | ASTM D-790 | 12000(11000) Mpa |
| Flexural Strength | dry(moist) | ASTM D-790 | 360(320) Mpa |
| Tensile Elongation?(Break) | dry(moist) | ASTM D-638 | 3(3) % |
| Other | Test Condition | Test Method | MITSUI CHEM JAPAN/A335K BK |
|---|---|---|---|
| Glass fiber content | 35 % |
| Electrical Properties | Test Condition | Test Method | MITSUI CHEM JAPAN/A335K BK |
|---|---|---|---|
| Dielectric Constant | 10 | ASTM D-150 | 4.5 |
| Dielectric breakdown voltage | dry | ASTM D-149 | 27 KV/mm |
| Loss factor | 10 | ASTM D-150 | 0.018 |
| Volume Resistivity | dry | ASTM D-257 | 10 Ω.cm |