Certificates
PC/ABS T90 XG COVESTRO SHANGHAI
Bayblend®
Automotive Applications、Electrical applications、household electrical appl
heat-resisting、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | COVESTRO SHANGHAI/T90 XG |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 57.0 J |
| 23°C | ISO 6603-2 | 51.0 J | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 无断裂 |
| Electrical performance | Test Condition | Test Method | COVESTRO SHANGHAI/T90 XG |
|---|---|---|---|
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 35 KV/mm |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.00 |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.10 |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 2.5E-03 |
| 23°C,1MHz | IEC 60250 | 0.010 |
| Mechanical properties | Test Condition | Test Method | COVESTRO SHANGHAI/T90 XG |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/50 | 61.0 Mpa |
| 断裂,23°C | ISO 527-2/50 | 56.0 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 5.1 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2400 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | >50 % |
| Filling analysis | Test Condition | Test Method | COVESTRO SHANGHAI/T90 XG |
|---|---|---|---|
| MeltViscosity | 260°C | ISO 11443-A | 225 Pa·s |
| physical property | Test Condition | Test Method | COVESTRO SHANGHAI/T90 XG |
|---|---|---|---|
| Shrinkage rate | TD:260°C,2.00mm | ISO 294-4 | 0.55-0.75 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| Shrinkage rate | MD:260°C,2.00mm | ISO 294-4 | 0.55-0.75 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.50 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 26.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | COVESTRO SHANGHAI/T90 XG |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 135 °C |
| Linear coefficient of thermal expansion | MD:23到55°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 130 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 112 °C | |
| vicat | -- | ISO 306/B50 | 134 °C |
| Linear coefficient of thermal expansion | TD:23到55°C | ISO 11359-2 | 7E-05 cm/cm/°C |