Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE PC4020 Malaysia ETILINAS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | Malaysia ETILINAS/PC4020 |
|---|---|---|---|
| Oxidation induction time (OIT) | 210℃ | ISO TR10837 | ＞20 min |
| Basic performance | Test Condition | Test Method | Malaysia ETILINAS/PC4020 |
|---|---|---|---|
| density | 退火 | ISO 1872/1 | 949 kg/m |
| melt mass-flow rate | 190℃/2.16kg | ISO 1133: Condition 4 | 0.3 g/10min |
| 190℃/5.0kg | ISO 1133: Condition 18 | 1.2 g/10min | |
| density | ISO 1183 | 947 kg/m | |
| Carbon black content | ISO 6964 | 2.25 % |
| Mechanical properties | Test Condition | Test Method | Malaysia ETILINAS/PC4020 |
|---|---|---|---|
| Shore hardness | ISO 868 (1sec) | 60 | |
| Tensile stress | ISO R527:Type 2 | 19 MPa | |
| elongation | 断裂 | ISO R527:Type 2 | ＞600 % |
| Flexural modulus | ISO 178 | 750 MPa | |
| Environmental stress cracking resistance | F0 | ASTM D-1693B | ＞1000 Hours |
| Electrical performance | Test Condition | Test Method | Malaysia ETILINAS/PC4020 |
|---|---|---|---|
| dielectric strength | ASTM D-149 | ＞25 kV/mm | |
| Volume resistivity | ASTM D-257 | ＞10 Ω.cm |
| Thermal performance | Test Condition | Test Method | Malaysia ETILINAS/PC4020 |
|---|---|---|---|
| vicat | ISO 306 A | 116 ℃ | |
| thermal conductivity | W/m℃ | BS 874(at 23℃) 0.4 | |
| brittle temperature | ASTM D-746 | ＜-100 ℃ |