HDPE SNOLEN® EF 3.3/54 JSC Gazprom neftekhim Salavat
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EF 3.3/54 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 6.0 kJ/m² |
| hardness | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EF 3.3/54 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 61 |
| film | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EF 3.3/54 |
|---|---|---|---|
| elongation | 断裂 | ISO 527-3/50 | 490 % |
| film thickness | 20to80µm | ||
| tensile strength | TD:断裂 | ISO 527-3/50 | 26.0 MPa |
| Dart impact | ASTM D1709 | 30 g | |
| Elmendorf tear strength | MD | 458.9 g/2.5cm | |
| tensile strength | MD:断裂 | ISO 527-3/50 | 41.0 MPa |
| Elmendorf tear strength | TD | 4920.1 g/2.5cm |
| Mechanical properties | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EF 3.3/54 |
|---|---|---|---|
| Tensile modulus | 23°C，正割 | ISO 527-2/1 | 1050 MPa |
| Tensile strain | 断裂 | ISO 527-2/50 | >1000 % |
| 屈服 | ISO 527-2/50 | 10 % | |
| tensile strength | 屈服 | ISO 527-2/50 | 25.0 MPa |
| 断裂 | ISO 527-2/50 | 30.0 MPa |
| physical property | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EF 3.3/54 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 0.950to0.954 g/cm³ |
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 2.5to3.3 g/10min |
| Melt flow ratio | 17.0to25.0 | ||
| Environmental stress cracking resistance | 80°C,2%Arkopal | ISO 16770 | 8.00 hr |
| melt mass-flow rate | 190°C/21.6kg | ISO 1133 | 55to65 g/10min |
| Thermal performance | Test Condition | Test Method | JSC Gazprom neftekhim Salavat/SNOLEN® EF 3.3/54 |
|---|---|---|---|
| vicat | ISO 306/B50 | 73.0 °C | |
| brittle temperature | ASTM D746 | <-80.0 °C |