Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL9330-4T8D028 SABIC INNOVATIVE CHONGQING
LEXAN™ Resin
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/EXL9330-4T8D028 |
|---|---|---|---|
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 50 kJ/m² |
| 23°C | ISO180/1A | 75 kJ/m² | |
| Unscented Izod Impact Strength 8 | 23°C | ISO180/1U | NoBreak |
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 50 kJ/m² |
| 23°C | ISO179/1eA | 70 kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO179/1eU | NoBreak |
| 23°C | ISO179/1eU | NoBreak |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/EXL9330-4T8D028 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 59.0 Mpa |
| Bending strength 5,6 | ISO178 | 86.0 Mpa | |
| elongation | 断裂 | ASTMD638 | 100 % |
| Tensile modulus | ASTMD638 | 2150 Mpa | |
| Tensile strain | 屈服 | ISO527-2/50 | 6.0 % |
| Tensile stress | 断裂 | ISO527-2/50 | 58.0 Mpa |
| elongation | 屈服 | ASTMD638 | 6.0 % |
| Tensile modulus | ISO527-2/1 | 2150 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 59.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 86.0 Mpa |
| tensile strength | 断裂 | ASTMD638 | 58.0 Mpa |
| Tensile strain | 断裂 | ISO527-2/50 | 100 % |
| Flexural modulus | ISO178 | 2150 Mpa | |
| 50.0mm跨距 | ASTMD790 | 2150 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/EXL9330-4T8D028 |
|---|---|---|---|
| CTI | IEC60112 | 250 V | |
| High arc combustion index (HAI) | HAI | UL746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 2 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/EXL9330-4T8D028 |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL94 | 5VB |
| GlowWireFlammability Index | 1.9mm | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 900 °C |
| UL flame retardant rating | 2.5mm | UL94 | 5VA |
| 0.8mm | UL94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/EXL9330-4T8D028 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.050 % |
| 饱和,23°C | ISO62 | 0.12 % | |
| density | ASTMD792 | 1.24 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 8.0 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 7.00 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.40to0.80 % |
| density | ISO1183 | 1.24 g/cm³ | |
| Outdoor applicability | UL746C | f1 |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/EXL9330-4T8D028 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 139 °C |
| Hot deformation temperature 10 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 126 °C |
| RTI Str | UL746 | 125 °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass |
| Hot deformation temperature 9 | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 139 °C |
| RTI Elec | UL746 | 125 °C | |
| vicat | ASTMD152511 | 147 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 126 °C |
| RTI Imp | UL746 | 110 °C | |
| vicat | -- | ISO306/B50 | 145 °C |
| -- | ISO306/B120 | 147 °C |