PA66 A218G2V30 BK SOLVAY FRANCE
TECHNYL®
Automotive sector
Thermal stability、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY FRANCE/A218G2V30 BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 87 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SOLVAY FRANCE/A218G2V30 BK |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1A | 10000 Mpa |
| Tensile strain | 断裂, 23°C | ISO 527-2 | 3.0 % |
| bending strength | 23°C | ISO 178 | 290 Mpa |
| Flexural modulus | 23°C | ISO 178 | 9200 Mpa |
| tensile strength | 断裂, 23°C | ISO 527-2/1A | 195 Mpa |
| flammability | Test Condition | Test Method | SOLVAY FRANCE/A218G2V30 BK |
|---|---|---|---|
| UL flame retardant rating | 1.6 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SOLVAY FRANCE/A218G2V30 BK |
|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.80 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.40 % |
| 横向流量 | ISO 294-4 | 1.1 % |
| Thermal performance | Test Condition | Test Method | SOLVAY FRANCE/A218G2V30 BK |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/Af | 250 °C |
| injection | Test Condition | Test Method | SOLVAY FRANCE/A218G2V30 BK |
|---|---|---|---|
| Suggested maximum moisture content | 0.15 % | ||
| Temperature in the middle of the barrel | 275 to 285 °C | ||
| Temperature at the rear of the barrel | 270 to 280 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 280 to 290 °C | ||
| Temperature | 70 to 100 °C |