Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC MN-3600HS CM70206HS TEIJIN JAPAN
PANLITE®
Lighting applications
heat-resisting,Flame retardant,Good impact resistance,Good liquidity,Halogen-free,Electrical field,Electronic field,Automotive sector
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TEIJIN JAPAN/MN-3600HS CM70206HS |
|---|---|---|---|
| density | ASTM D792 | 1.19 g/cm³ |
| thermal performance | Test Condition | Test Method | TEIJIN JAPAN/MN-3600HS CM70206HS |
|---|---|---|---|
| elongation at yield | ISO 527-2/50 | 7 % | |
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 125 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 112 °C | |
| Linear coefficient of thermal expansion | 流动 | ASTM D696 | 0.000070 cm/cm/°C |
| 横动 | ASTM D696 | 0.000070 cm/cm/°C | |
| tensile strength | 断裂 | ISO 527-2/5 | 50 Mpa |
| mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/MN-3600HS CM70206HS |
|---|---|---|---|
| bending strength | ISO 178 | 95 Mpa | |
| Elongation at break | ISO 527-2/50 | 50 % | |
| flexural modulus | ISO 178 | 2300 Mpa | |
| Tensile modulus | ISO 527-2/1 | 2350 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 60 Mpa |
| Water absorption rate | 23℃, 24 hr | ISO 62 | 0.22 % |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/MN-3600HS CM70206HS |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1000000000000000 ohms | |
| Thermal performance | 测试条件 | 测试方法 | 属性值 单位 |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/MN-3600HS CM70206HS |
|---|---|---|---|
| melt mass-flow rate | 280℃/2.16 kg | ISO 1133 | 17 g/10 min |
| shrinkage rate | 横向流量 : 4.00 mm | ISO 294-4 | 0.5-0.7 % |
| 流量 : 4.00 mm | ISO 294-4 | 0.5-0.7 % |
| flammability | Test Condition | Test Method | TEIJIN JAPAN/MN-3600HS CM70206HS |
|---|---|---|---|
| UL flame retardant rating | 1.00 mm | UL 94 | V-1 无 |
| 2.00 mm | UL 94 | 5VB 无 | |
| 1.50 mm | UL 94 | V-0 无 |