ABS SE-3 MITSUBISHI RAYON AMERICA
--
Electrical components
Good chemical resistance, dimensional stability, impact resistance, good processability, toughness, high hardness, high rigidity, high strength, and processability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/SE-3 |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D-570 | 0.30 % |
| melt mass-flow rate | 200℃/5.0kg | ASTM D-1238 | 1.2 g/10min |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/SE-3 |
|---|---|---|---|
| tensile strength | 屈服,23℃ | ASTM D-638 | 44.1 MPa |
| bending strength | 23℃，6.35mm，屈服 | ASTM D-790 | 66.7 MPa |
| Tensile modulus | 23℃ | ASTM D-638 | 2350 MPa |
| Impact strength of cantilever beam gap | 23℃，6.35mm | ASTM D-256 | 216 J/m |
| Rockwell hardness | ASTM D-785 | 107 R-Scale | |
| Impact strength of cantilever beam gap | -40℃，6.35mm | ASTM D-256 | 58.8 J/m |
| Flexural modulus | 23℃，6.35mm | ASTM D-790 | 2450 MPa |
| Impact strength of cantilever beam gap | 0℃，6.35mm | ASTM D-256 | 157 J/m |
| physical property | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/SE-3 |
|---|---|---|---|
| density | ASTM D-792 | 1.05 g/cm | |
| Shrinkage rate | Flow | ASTM D-955 | 0.50 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/SE-3 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa，未退火，12.7mm，HDT | ASTM D-648 | 92.0 ℃ |
| specific heat | ASTM C-351 | 1670 J/kg/℃ | |
| Linear coefficient of thermal expansion | Flow | ASTM D-696 | 0.000085 cm/cm/℃ |
| thermal conductivity | ASTM C-177 | 0.21 W/m.K |