ABS 500 TORAY JAPAN
Toyolac® 
Automotive sector、Electronic field、Electrical field
High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Basic performanceTest ConditionTest MethodTORAY JAPAN/500
melt mass-flow rate220℃/98NISO 113320 g/10min
Mechanical propertiesTest ConditionTest MethodTORAY JAPAN/500
Impact strength of cantilever beam gapASTM D256/ISO 17978 kg·cm/cm(J/M)ft·lb/in
bending strengthASTM D790/ISO 17889 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap23℃ 3.2mmASTM D-25698 J/m
Flexural modulusASTM D790/ISO 1782690 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap-23℃ 12.7mmASTM D-25669 J/m
elongationASTM D638/ISO 52712 %
Impact strength of cantilever beam gap0℃ 3.2mmASTM D-25698 J/m
bending strength23℃ 50RHASTM D-79081 Mpa
Impact strength of cantilever beam gap23℃ 12.7mmASTM D-256137 J/m
Rockwell hardness23℃ 50RHASTM D-785116 R-Scale
ASTM D785116
tensile strength ASTM D638/ISO 52759 kg/cm²(MPa)[Lb/in²]
Flexural modulus23℃ 50RHASTM D-7902600 Mpa
elongation断裂ASTM D-63837 %
tensile strength 23℃ 50RHASTM D-63854 Mpa
Impact strength of cantilever beam gap-30℃,3.2mmASTM D-25678 J/m
0℃ 12.7mmASTM D-25698 J/m
Physical propertiesTest ConditionTest MethodTORAY JAPAN/500
Shrinkage rateASTM D9550.4-0.6 %
densityASTM D792/ISO 11831.05
melt mass-flow rateASTM D1238/ISO 113320 g/10min
physical property Test ConditionTest MethodTORAY JAPAN/500
Shrinkage rate0.4-0.6 %
Thermal performanceTest ConditionTest MethodTORAY JAPAN/500
Combustibility (rate)UL 94HB
Linear coefficient of thermal expansionASTM D-6966.9
Heat distortion temperature1.82Mpa，HDTASTM D-64888 °C
Linear coefficient of thermal expansionASTM D696/ISO 113596.9×10^-5 mm/mm.℃
Ball indentation temperature95 °C
UL flame retardant ratingUL 94HB