PPS OF-1006 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and electrical
Flame retardant、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/OF-1006 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 24 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.36 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.9 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/OF-1006 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 12000 Mpa | |
| ASTM D638 | 12100 Mpa | ||
| tensile strength | 断裂 | ISO 527-2/5 | 126 Mpa |
| elongation | 断裂 | ASTM D638 | 1.5 % |
| bending strength | ISO 178 | 175 Mpa | |
| Flexural modulus | ISO 178 | 10500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 1.3 % |
| tensile strength | 断裂 | ASTM D638 | 132 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 10000 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 170 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/OF-1006 |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.10-0.30 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.024 % |
| 平衡,23°C,50%RH | ISO 62 | 0.067 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.70-0.90 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/OF-1006 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 275 °C |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 2.2E-05 cm/cm/°C |
| TD：-30to30°C | ASTM D696 | 4.5E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 276 °C |
| 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 258 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 261 °C |