density

ASTMD792

g/cm³

1

density

ISO1183

g/cm³

1

Melt Volume-Flow Rate (MVR)

200°C/5.0kg

ISO1133

cm3/10min

1

Melt mass flow rate

200°C/5.0kg

ASTMD1238

g/10min

1

Shrinkage rate

MD

ASTMD955

%

0

Shrinkage rate

ISO294-4

%

0

Water absorption rate

饱和,23°C

ASTMD570

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

InstrumentedDartImpact

Totalenergy

ASTMD3763

J

2

Nominal tensile fracture strain

23°C

ISO527-2

%

1

Charpy Notched Impact Strength

23°C

ISO179

kJ/m²

3

Tensile modulus

ASTMD638

Mpa

1

Tensile modulus

ISO527-2

Mpa

1

tensile strength

屈服,23°C

ASTMD638

Mpa

2

tensile strength

屈服,23°C

ISO527-2

Mpa

2

elongation

屈服,23°C

ISO527-2

%

2

elongation

断裂

ASTMD638

%

2

Bending modulus

ASTMD790

Mpa

1

Bending modulus

ISO178

Mpa

1

bending strength

ASTMD790

Mpa

2

bending strength

--

ISO178

Mpa

3

Impact strength of cantilever beam gap

23°C

ASTMD256

J/m

3

Impact strength of cantilever beam gap

-30°C

ISO180/A

kJ/m²

2

Impact strength of cantilever beam gap

23°C

ISO180/A

kJ/m²

3

Hot deformation temperature

0.45MPa,未退火

ASTMD648

°C

7

Hot deformation temperature

0.45MPa,Annealed

ISO75-2/B

°C

7

Hot deformation temperature

1.8MPa,未退火

ASTMD648

°C

6

Hot deformation temperature

1.8MPa,退火

ISO75-2/A

°C

5

vicat softening point

ASTMD15253

°C

8

vicat softening point

--

ISO306/A50

°C

8

vicat softening point

--

ISO306/B50

°C

5

Linear coefficient of thermal expansion

MD

ASTMD696

cm/cm/°C

1

Linear coefficient of thermal expansion

MD

ISO11359-2

cm/cm/°C

6

Surface resistivity

ASTMD257

ohms

>

Surface resistivity

IEC60093

ohms

1

Leakage Trace Index

IEC60112

V

6

Volume resistivity

ASTMD257

ohms·cm

>

Volume resistivity

IEC60093

ohms·cm

>

Elongation MD

断裂

ISO527-3

%

1

Light transmittance

550nm

ASTMD1003

%

9

Haze

ASTMD1003

%

0