Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LLDPE CA3817 Cabot Corporation
--
Packaging, electrical components
Conductive
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | Cabot Corporation/CA3817 |
|---|---|---|---|
| tensile strength | MD:断裂,100µm | ISO 527-3/500 | 25.1 MPa |
| elongation | TD:断裂,100µm | ISO 527-3/500 | 940 % |
| tensile strength | TD:屈服,100µm | ISO 527-3/500 | 11.5 MPa |
| elongation | MD:断裂,100µm | ISO 527-3/500 | 1100 % |
| Tear resistance of pants | MD:50µm | ASTM D1938 | 106 N/mm |
| tensile strength | TD:断裂,100µm | ISO 527-3/500 | 22.4 MPa |
| Tear resistance of pants | TD:50µm | ASTM D1938 | 104 N/mm |
| tensile strength | MD:屈服,100µm | ISO 527-3/500 | 11.8 MPa |
| Electrical performance | Test Condition | Test Method | Cabot Corporation/CA3817 |
|---|---|---|---|
| Surface Resistivity | 0.100 mm | 内部方法 | 1E+04 ohm |
| 0.100mm | 内部方法 | 1E+04 ohms |
| Mechanical properties | Test Condition | Test Method | Cabot Corporation/CA3817 |
|---|---|---|---|
| tensile strength | TD : 100 µm | 22.4 MPa | |
| Tear resistance of pants | TD : 50 µm | 104 N/mm | |
| MD : 50 µm | ASTM D1938 | 106 N/mm | |
| elongation | MD : 断裂, 100 µm | ISO 527-3/500 | 1100 % |
| TD : 断裂, 100 µm | 940 % | ||
| tensile strength | TD : 屈服, 100 µm | 11.5 MPa | |
| MD : 100 µm | 25.1 MPa | ||
| Flexural modulus | 模压成型 | ISO 178 | 284 MPa |
| tensile strength | MD : 屈服, 100 µm | ISO 527-3/500 | 11.8 MPa |
| physical property | Test Condition | Test Method | Cabot Corporation/CA3817 |
|---|---|---|---|
| Flexural modulus | 模压成型 | ISO 178 | 284 MPa |
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 2.0 g/10min |
| 190°C/10.0kg | ISO 1133 | 6.0 g/10min | |
| density | 23°C | 内部方法 | 1.04 g/cm³ |
| melt mass-flow rate | 190°C/10.0 kg | ISO 1133 | 6.0 g/10 min |
| density | 内部方法 | 1.04 g/cm3 | |
| melt mass-flow rate | 190°C/21.6 kg | 2.0 g/10 min |