Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PMMA VH001 MITSUBISHI NANTONG
ACRYPET™
Household appliances、Household appliances、Casters、Optical level、vehicle、lighting、Optical Products
UV resistance、standard、High temperature resistan、Weather resistance、transparent、Has the best heat resista、Climate resistance
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | MITSUBISHI NANTONG/VH001 |
|---|---|---|---|
| Water absorption rate | 24hr | ISO 62 | 0.3 % |
| melt mass-flow rate | 230℃,37.3N | ISO 1133 | 2.0 g/10min |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI NANTONG/VH001 |
|---|---|---|---|
| Tensile modulus | 1A/1 | ISO 527-2 | 3.3 GPa |
| elongation | 1A/5 | ISO 527-2 | 6 % |
| bending strength | ISO 178 | 127 Mpa | |
| Impact strength of cantilever beam gap | 1eA V槽口 | JIS K-7111 | 1.3 KJ/m |
| Rockwell hardness | ISO 2039 | 101 M Scale | |
| Flexural modulus | ISO 178 | 3.3 GPa | |
| Impact strength of cantilever beam gap | 1A | JIS K-7110 | 1.7 KJ/m |
| 1eU 无槽口 | JIS K-7111 | 21 KJ/m | |
| tensile strength | 1A/5 | ISO 527-2 | 78 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI NANTONG/VH001 |
|---|---|---|---|
| dielectric loss tangent | 60Hz | JIS K-6911 | 0.05 |
| Volume resistivity | JIS K-6911 | >10 Ω | |
| JIS K-6911 | >10 Ωm | ||
| dielectric strength | 4kV/sec | JIS K-6911 | 20 MV/m |
| arc resistance | JIS K-6911 | 没有痕迹 | |
| dielectric constant | 60Hz | JIS K-6911 | 3.7 |
| physical property | Test Condition | Test Method | MITSUBISHI NANTONG/VH001 |
|---|---|---|---|
| Haze ratio | 3mm | ISO 14782 | 0.3 % |
| density | ISO 1183 | 1.19 g/cm | |
| refractive index | N | ISO 489 | 1.49 |
| transmittance | 3mm | ISO 13468-1 | 93 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI NANTONG/VH001 |
|---|---|---|---|
| specific heat | JIS K-7123 | 1.5 J/(g·℃) | |
| Linear coefficient of thermal expansion | JIS K-7197 | 6×10 1/℃ | |
| spiral flow length | 厚薄2mm,250℃ | 三菱丽阳法 | 220 mm |
| vicat | 50n | ISO 306 | 108 °C |
| Heat distortion temperature | 1.80MPa | ISO 75-2 | 101 °C |
| Heat transfer rate | JIS A-1412 | 0.2 W/(m·℃) | |
| spiral flow length | 厚薄2mm,230℃ | 三菱丽阳法 | 130 mm |