PPO/PA GTX973-74709 SABIC INNOVATIVE US
NORYL GTX™
Electrical applications、Industrial machinery
High mobility、dimensional stability 、High temperature resistan、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX973-74709 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| Dart impact | -30°C,EnergyatPeakLoad | ASTM D3763 | 36.0 J |
| Suspended wall beam without notch impact strength | -30°C | ASTM D4812 | 3200 J/m |
| -40°C | ASTM D4812 | 3200 J/m | |
| Dart impact | -40°C,EnergyatPeakLoad | ASTM D3763 | 19.7 J |
| 23°C,EnergyatPeakLoad | ASTM D3763 | 46.1 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/GTX973-74709 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/GTX973-74709 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 52 % |
| 屈服 | ASTM D638 | 9.0 % | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 19.0 mg |
| tensile strength | 断裂 | ASTM D638 | 56.5 Mpa |
| 屈服 | ASTM D638 | 60.0 Mpa | |
| bending strength | 屈服,100mm跨距 | ASTM D790 | 89.6 Mpa |
| Flexural modulus | 100mm跨距 | ASTM D790 | 2240 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/GTX973-74709 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/GTX973-74709 |
|---|---|---|---|
| Shrinkage rate | MD:130°C,1小时 | ASTM D955 | 1.1-1.5 % |
| Water absorption rate | 24hr | ASTM D570 | 0.40 % |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.90-1.2 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 3.6 % |
| Shrinkage rate | TD:3.20mm | 内部方法 | 0.80-1.1 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX973-74709 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 128 °C |
| Linear coefficient of thermal expansion | MD：-20到150°C | ASTME831 | 9E-05 cm/cm/°C |
| vicat | -- | ASTM D15255 | 233 °C |
| -- | ASTM D15256 | 232 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 156 °C |
| RTI Imp | UL 746 | 50.0 °C | |
| RTI | UL 746 | 50.0 °C | |
| RTI Elec | UL 746 | 50.0 °C |