ABS AG23AT FORMOSA NINGBO
TAIRILAC®
Car wheel housing cover、Phone case、Nameplate
Electroplated、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | FORMOSA NINGBO/AG23AT |
|---|---|---|---|
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 108 |
| R 级, 23°C | ASTM D785 | 108 |
| Mechanical properties | Test Condition | Test Method | FORMOSA NINGBO/AG23AT |
|---|---|---|---|
| Flexural modulus | 23°C | ASTM D790, ISO 178 | 2350 Mpa |
| tensile strength | 23°C | ASTM D638, ISO 527-2 | 44.0 Mpa |
| bending strength | 23°C | ASTM D790, ISO 178 | 74.0 Mpa |
| flammability | Test Condition | Test Method | FORMOSA NINGBO/AG23AT |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm, All Colors | UL 94 | HB |
| physical property | Test Condition | Test Method | FORMOSA NINGBO/AG23AT |
|---|---|---|---|
| melt mass-flow rate | 220°C/10.0 kg | ASTM D1238, ISO 1133 | 19 g/10 min |
| 200°C/5.0 kg | ASTM D1238, ISO 1133 | 1.9 g/10 min |
| Thermal performance | Test Condition | Test Method | FORMOSA NINGBO/AG23AT |
|---|---|---|---|
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 12.7 mm | ASTM D648, ISO 75-2/A | 84.0 °C |
| 1.8 MPa, 退火 3 | ASTM D648, ISO 75-2/A | 94.0 °C | |
| vicat | ISO 306/A, ASTM D15254 | 100 °C |
| injection | Test Condition | Test Method | FORMOSA NINGBO/AG23AT |
|---|---|---|---|
| Temperature | 40 到 80 °C | ||
| Processing (melt) temperature | 190 到 230 °C | ||
| drying temperature | 70 到 80 °C | ||
| Injection Pressure | 68.6 到 108 Mpa | ||
| drying time | 2.0 到 3.0 hr |