Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EF1006FH WA407 LG GUANGZHOU
LUPOY®
OA device、Phone Case、Electrical applications、Electrical/Electronic App
heat-resisting、Flame retardant、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG GUANGZHOU/EF1006FH WA407 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 760 J/m |
| hardness | Test Condition | Test Method | LG GUANGZHOU/EF1006FH WA407 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | LG GUANGZHOU/EF1006FH WA407 |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | >100 % |
| tensile strength | 屈服,3.20mm | ASTM D638 | 61.8 Mpa |
| Flexural modulus | 3.20mm | ASTM D790 | 2260 Mpa |
| bending strength | 屈服,3.20mm | ASTM D790 | 95.1 Mpa |
| flammability | Test Condition | Test Method | LG GUANGZHOU/EF1006FH WA407 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.0mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LG GUANGZHOU/EF1006FH WA407 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.50-0.70 % |
| density | ASTM D792 | 1.21 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | LG GUANGZHOU/EF1006FH WA407 |
|---|---|---|---|
| vicat | ASTM D15255 | 140 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 130 °C |
| RTI Imp | UL 746 | 115 °C | |
| RTI Str | UL 746 | 120 °C | |
| RTI Elec | UL 746 | 120 °C |