PES JX89626 SABIC INNOVATIVE US
LNP™ STAT-KON™ 
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/JX89626
Suspended wall beam without notch impact strength23°CISO 180/1U37 kJ/m²
Dart impact23°C,TotalEnergyASTM D37637.30 J
Multi axis Instrumented Impact EnergyISO 6603-23.80 J
Impact strength of cantilever beam gap23°CISO 180/1A6.1 kJ/m²
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/JX89626
Surface ResistivityASTM D2572.0to5.0 ohms
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/JX89626
Tensile modulusISO 527-2/111200 Mpa
ASTM D63811900 Mpa
tensile strength 断裂ISO 527-2/5161 Mpa
elongation断裂ASTM D6382.1 %
bending strengthISO 178226 Mpa
Flexural modulusISO 1789680 Mpa
Tensile strain断裂ISO 527-2/52.2 %
tensile strength 断裂ASTM D638163 Mpa
Flexural modulus50.0mm跨距ASTM D79010100 Mpa
bending strength断裂,50.0mm跨距ASTM D790238 Mpa
physical property Test ConditionTest MethodSABIC INNOVATIVE US/JX89626
Shrinkage rateMD：24小时ASTM D9550.10-0.30 %
Water absorption rate24hr,50%RHASTM D5700.49 %
平衡,23°C,50%RHISO 620.71 %
Shrinkage rateTD：24hrASTM D9550.50-0.80 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/JX89626
Heat distortion temperature0.45MPa,Unannealed,64.0mmSpan，HDTISO 75-2/Bf219 °C
Linear coefficient of thermal expansionMD：-30到30°CASTM D6964.7E-05 cm/cm/°C
TD：-30to30°CASTM D6963.8E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,3.20mm，HDTASTM D648220 °C
1.8MPa,未退火,64.0mm跨距，HDTISO 75-2/Af214 °C
1.8MPa,未退火,3.20mm，HDTASTM D648214 °C