PC PC-115 TAIWAN CHIMEI
WONDERLITE®
Casters
Low viscosity、transparent
MSDS
RoHS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIWAN CHIMEI/PC-115 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 850 J/m |
| 23°C | ISO180/1A | 70 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO179 | 70 kJ/m² |
| hardness | Test Condition | Test Method | TAIWAN CHIMEI/PC-115 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTMD785 | 77 |
| Mechanical properties | Test Condition | Test Method | TAIWAN CHIMEI/PC-115 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/50 | 70.0 Mpa |
| 屈服 | ISO527-2/50 | 64.0 Mpa | |
| elongation | 断裂 | ASTMD638 | 110 % |
| Flexural modulus | ASTMD790 | 2340 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 61.6 Mpa |
| Tensile strain | 断裂 | ISO527-2/50 | 120 % |
| Flexural modulus | ISO178 | 2400 Mpa | |
| Bending stress 5 | ISO178 | 90.0 Mpa | |
| bending strength | ASTMD790 | 89.8 Mpa |
| flammability | Test Condition | Test Method | TAIWAN CHIMEI/PC-115 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-2 |
| 2.5mm | UL94 | V-2 |
| physical property | Test Condition | Test Method | TAIWAN CHIMEI/PC-115 |
|---|---|---|---|
| Density/specific gravity 2 | ASTMD792 | 1.20 g/cm³ | |
| density | 23°C | ISO1183 | 1.20 g/cm³ |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 15.0 cm3/10min |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 15 g/10min |
| Shrinkage rate | ISO294-4 | 0.50to0.70 % |
| Thermal performance | Test Condition | Test Method | TAIWAN CHIMEI/PC-115 |
|---|---|---|---|
| Hot deformation temperature 6 | 0.45MPa,Annealed | ASTMD648 | 145 °C |
| Heat distortion temperature | 1.8MPa,退火 | ISO75-2/A | 143 °C |
| vicat | -- | ISO306/A50 | 150 °C |
| MD | ISO11359-2 | 6.0E-5to8.0E-5 cm/cm/°C | |
| vicat | ASTMD15257 | 150 °C | |
| Heat distortion temperature | 1.8MPa,未退火 | ISO75-2/A | 128 °C |
| vicat | -- | ISO306/B50 | 145 °C |