Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PK LUVOCOM® 70-9046 LEHVOSS Group
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 70-9046 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 22 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1fU | 72 kJ/m² |
| Electrical performance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 70-9046 |
|---|---|---|---|
| insulation resistance | IEC 60167 | >1.0E+11 ohms | |
| Surface Resistivity | IEC 60093 | >1.0E+11 ohms |
| Mechanical properties | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 70-9046 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 1400 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 50.0 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 40 % |
| Flexural modulus | ISO 178 | 1200 MPa | |
| bending strength | ISO 178 | 65.0 MPa |
| physical property | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 70-9046 |
|---|---|---|---|
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 5.00 cm³/10min |
| Shrinkage rate | DIN 16901 | 1.6to2.2 % | |
| Water absorption rate | 23°C,24hr | 0.15 % | |
| density | ISO 1183 | 1.33 g/cm³ |
| Thermal performance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 70-9046 |
|---|---|---|---|
| Continuous use temperature | UL 746B | 90.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C |
| vicat | ISO 306/A | 200 °C | |
| maximum service temperature | ShortTerm | 120 °C |