PC GZ2540 IDEMITSU JAPAN
TARFLON™
Automotive Applications,Home appliance components
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | IDEMITSU JAPAN/GZ2540 |
---|---|---|---|
Rockwell hardness | M级 | ISO 2039-2 | 75 |
Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/GZ2540 |
---|---|---|---|
ISO Shortcut | >PC-GF40< |
Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/GZ2540 |
---|---|---|---|
bending strength | ASTM D790/ISO 178 | 185 kg/cm²(MPa)[Lb/in²] | |
Flexural modulus | ASTM D790/ISO 178 | 11.3 kg/cm²(MPa)[Lb/in²] | |
Charpy Notched Impact Strength | ISO 179 | 11 kJ/m² | |
tensile strength | 断裂 | ISO 527-2 | 130 Mpa |
elongation at break | ASTM D638/ISO 527 | 2 % | |
Rockwell hardness | ASTM D785 | M75 | |
tensile strength | ASTM D638/ISO 527 | 130 kg/cm²(MPa)[Lb/in²] | |
Nominal tensile fracture strain | ISO 527-2 | 2.0 % | |
bending strength | ISO 178 | 185 Mpa | |
Tensile strain | 断裂 | ISO 527-2 | 2 % |
Flexural modulus | ISO 178 | 11300 Mpa | |
tensile strength | 屈服 | ISO 527-2 | 130 Mpa |
Rockwell hardness | M 计秤 | ISO 2039-2 | 75 |
Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/GZ2540 |
---|---|---|---|
Volume resistivity | ASTM D257 | >1.0E+16 ohms·cm | |
dielectric strength | IEC 60243-1 | >22 KV/mm | |
dielectric constant | ASTM D150/IEC 60250 | 2.95 | |
1MHz | IEC 60250 | 3.45 | |
arc resistance | ASTM D495/IEC 60112 | 110 | |
dielectric constant | 1 MHz | IEC 60250 | 2.95 |
arc resistance | ASTM D495 | 110 sec | |
Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
other | Test Condition | Test Method | IDEMITSU JAPAN/GZ2540 |
---|---|---|---|
characteristic | GF增强/非溴/非磷/阻燃 V-0 | ||
purpose | 打印机和复印机零部件、液晶投影仪零部件、手机外壳、电动工具、游戏机外壳 |
Physical properties | Test Condition | Test Method | IDEMITSU JAPAN/GZ2540 |
---|---|---|---|
Shrinkage rate | ASTM D955 | 0.12-0.6 % | |
density | ASTM D792/ISO 1183 | 1.51 | |
Water absorption rate | ASTM D570/ISO 62 | 0.1 % |
flammability | Test Condition | Test Method | IDEMITSU JAPAN/GZ2540 |
---|---|---|---|
UL flame retardant rating | 3.0mm | UL 94 | V-0 |
2.0mm | UL 94 | V-1 | |
1.5mm | UL 94 | V-0 |
physical property | Test Condition | Test Method | IDEMITSU JAPAN/GZ2540 |
---|---|---|---|
Shrinkage rate | TD:2.00mm | 内部方法 | 0.60 % |
MD: 2.00 mm | 内部方法 | 0.12 % | |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
Shrinkage rate | TD | 内部方法 | 0.6 % |
MD:2.00mm | 内部方法 | 0.12 % | |
Water absorption rate | 平衡, 23℃, 50% RH | ISO 62 | 0.1 % |
Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/GZ2540 |
---|---|---|---|
Combustibility (rate) | UL 94 | V-0/1.5(black) | |
Heat distortion temperature | HDT | ASTM D648/ISO 75 | 147 ℃(℉) |
1.8 MPa, 未退火,HDT | ISO 75-2/A | 147 °C | |
1.8MPa,未退火,HDT | ISO 75-2/A | 147 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.9E-05 cm/cm/°C |
UL flame retardant rating | 1.50 mm | UL 94 | V-0 |
Linear coefficient of thermal expansion | ASTM D696 | 0.000019 cm/cm/℃ | |
ASTM D696/ISO 11359 | 1.9 mm/mm.℃ |