Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 AKV25F30 900864 ENVALIOR WUXI
Durethan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ENVALIOR WUXI/AKV25F30 900864 |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 3.00 J |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 900 N |
| -30°C | ISO180/1U | 45 kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 1.90 J |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO6603-2 | 1000 N |
| 23°C | ISO180/1U | 50 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 55 kJ/m² |
| -30°C | ISO179/1eU | 45 kJ/m² |
| Supplementary Information | Test Condition | Test Method | ENVALIOR WUXI/AKV25F30 900864 |
|---|---|---|---|
| ISO Shortcut | ISO1874 | PA6,GFHR,14-110,GF25 |
| Electrical performance | Test Condition | Test Method | ENVALIOR WUXI/AKV25F30 900864 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 4.1E+13 ohms | |
| Volume resistivity | 23°C | IEC60093 | 3.4E+14 ohms·cm |
| CTI | 解决方案A | IEC60112 | 400 V |
| Mechanical properties | Test Condition | Test Method | ENVALIOR WUXI/AKV25F30 900864 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO178/A | 10000 Mpa |
| Bending stress | 23°C | ISO178/A | 230 Mpa |
| 23°C | ISO178/A | 2.5 % | |
| Tensile strain | 断裂,23°C | ISO527-2/5 | 2.3 % |
| Tensile stress | 断裂,23°C | ISO527-2/5 | 150 Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 11000 Mpa |
| flammability | Test Condition | Test Method | ENVALIOR WUXI/AKV25F30 900864 |
|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL94 | V-0 |
| Burning wire flammability index | 0.8mm | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.40mm | IEC60695-2-13 | 850 °C |
| 3.0mm | IEC60695-2-13 | 850 °C | |
| UL flame retardant rating | 3.0mm | UL94 | V-0 |
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 960 °C |
| BurningBehavior7 | ISO3795 | passed | |
| Burning wire flammability index | 0.40mm | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.8mm | IEC60695-2-13 | 775 °C |
| 1.5mm | IEC60695-2-13 | 775 °C | |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 °C |
| UL flame retardant rating | 0.40mm | UL94 | V-0 |
| physical property | Test Condition | Test Method | ENVALIOR WUXI/AKV25F30 900864 |
|---|---|---|---|
| Shrinkage rate | TD:280°C,2.00mm2 | ISO2577 | 0.60 % |
| MD:280°C,2.00mm2 | ISO2577 | 0.30 % | |
| MD:120°C,4小时,2.00mm3 | ISO2577 | 0.10 % | |
| TD:120°C,4小时,2.00mm3 | ISO2577 | 0.10 % |
| Thermal performance | Test Condition | Test Method | ENVALIOR WUXI/AKV25F30 900864 |
|---|---|---|---|
| 0.45MPa,未退火 | ISO75-2/B | 215 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 205 °C | |
| Melting temperature 5 | ISO11357-3 | 222 °C | |
| vicat | ISO306/B120 | 205 °C | |
| TD：23to55°C | ISO11359-2 | 9E-05 cm/cm/°C | |
| MD：23到55°C | ISO11359-2 | 2E-05 cm/cm/°C |