PEI EX12310C BKNAT SABIC INNOVATIVE US
LNP™ STAT-KON™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EX12310C BKNAT |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 3.6 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EX12310C BKNAT |
|---|---|---|---|
| --2 | ASTM D638 | 9170 Mpa | |
| fracture | ISO 527-2/5 | 156 Mpa | |
| ASTM D638 | 2.4 % | ||
| --6 | ISO 178 | 8410 Mpa | |
| fracture | ASTM D638 | 158 Mpa | |
| 50.0mm span | ASTM D790 | 8140 Mpa | |
| fracture | ISO 527-2/5 | 2.3 % | |
| --7 | ISO 178 | 225 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 224 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/EX12310C BKNAT |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 5.1E+05 ohms·cm | |
| Surface Resistivity | ASTM D257 | 4E+05 ohms |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/EX12310C BKNAT |
|---|---|---|---|
| UL flame retardant rating | 0.600mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/EX12310C BKNAT |
|---|---|---|---|
| Shrinkage rate | TD:24小时 | ASTM D955 | 0.50-0.70 % |
| melt mass-flow rate | 367°C/6.6kg | ASTM D1238 | 31 g/10min |
| Shrinkage rate | MD:24小时 | ASTM D955 | 0.20-0.40 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EX12310C BKNAT |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:40到120°C | ASTME831 | 6.3E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 201 °C | |
| Linear coefficient of thermal expansion | MD:40到120°C | ASTME831 | 1.6E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 6.40mm | ASTM D648 | 197 °C |