Product Name / Manufacturer / Model

Brand

Typical Applications

Properties

Color

Form

Processing Methods

Grade

Filler

Recycled Content

Certificates

Reference Price

TPV
TPV CELANESE USA 291-60B150
Weather resistant grade
US$ 8,200 / MT
FOB Guangzhou port, China
agingTest ConditionTest MethodCELANESE USA/291-60B150
Quality change rate23.0°C,168hr,inSodiumHydroxide,50%ISO 18170.10 %
23°C,168hr,inSodiumChloride,15%ASTM D4710.10 %
Hardness change rate in the airShoreA,100°C,672hrASTM D573-2.0
Volume change23°C,168hr,inSodiumChloride,15%ASTM D4710.60 %
Change rate of tensile strength in air23°C,168hr,inClorox,10%ASTM D471-16 %
Tensile stress change rate23°C,24hr,inIRM903Oil，BreakISO 1817-4.0-4.0-4.0-4.0-4.0 %
Quality change rate38°C,168hr,inRelativeHumidity,95%ASTM D4710.60 %
23.0°C,168hr,inHydrochloricAcid,10%ISO 18170.40 %
23.0°C,168hr,inRelativeHumidity,95%ISO 18170.0 %
Change rate of ultimate elongation in air23°C,24hr,inIRM903OilASTM D471-4.0-4.0-4.0-4.0-4.0 %
Volume change23°C,168hr,inRelativeHumidity,95%ASTM D4710.0 %
Change rate of ultimate elongation in air23°C,168hr,inHydrochloricAcid,10%ASTM D471-10 %
23°C,168hr,inCascadeDetergentASTM D471-7.0 %
38°C,168hr,inRelativeHumidity,90%ASTM D471-9.0 %
Change rate of tensile strength in air23°C,168hr,inHydrochloricAcid,10%ISO 1817-20 %
Tensile stress change rate23°C,168hr,inSodiumChloride,15%，BreakISO 1817-6.0 %
Quality change rate23.0°C,168hr,inClorox,10%ISO 18170.60 %
Change rate of tensile strength in air23°C,168hr,inClorox,10%ISO 1817-16 %
38°C,168hr,inRelativeHumidity,90%ASTM D471-16 %
Volume change23°C,168hr,inSodiumChloride,15%ISO 18170.60 %
23°C,168hr,inCascadeDetergentISO 18170.10 %
23°C,168hr,inClorox,10%ASTM D4710.60 %
Change rate of tensile strength in air23°C,168hr,inHydrochloricAcid,10%ASTM D471-20 %
Tensile stress change rate23°C,168hr,inRelativeHumidity,90%，BreakISO 1817-10 %
Change rate of tensile strength in air23°C,24hr,inIRM903OilISO 1817-4.0 %
23°C,168hr,inSodiumChloride,15%ASTM D471-18 %
Volume change23°C,168hr,inCascadeDetergentASTM D4710.10 %
Quality change rate23°C,168hr,inRelativeHumidity,95%ASTM D4710.0 %
Tensile stress change rate38°C,168hr,inRelativeHumidity,90%，BreakISO 1817-9.0 %
Shore hardnessShoreA,23°C,168hr,inDeionizedWaterISO 1817-1.0
Change rate of tensile strength in air100°C,168hrISO 1880.0 %
Elongation at Break100°C,168hrASTM D573-11 %
Change rate of ultimate elongation in air23°C,168hr,inRelativeHumidity,90%ASTM D471-10 %
23°C,168hr,inEthanol,50%ASTM D471-66 %
Quality change rate23°C,168hr,inCascadeDetergentASTM D4710.10 %
Volume change23°C,168hr,inRelativeHumidity,95%ISO 18170.0 %
Change rate of ultimate elongation in air23°C,168hr,inSodiumChloride,15%ASTM D471-6.0 %
Change rate of tensile strength in air23°C,168hr,inEthanol,50%ISO 1817-65 %
Changes in air quality100°C,168hrASTM D573-1.1 %
Quality change rate23.0°C,168hr,inSodiumChloride,15%ISO 18170.10 %
Change rate of tensile strength in air23°C,168hr,inSodiumHydroxide,50%ISO 1817-22 %
Changes in air quality100°C,168hrISO 188-1.1 %
Tensile stress change rate23°C,168hr,inSodiumHydroxide,50%，BreakISO 1817-18 %
Change rate of tensile strength in air100°C,168hrASTM D5730.0 %
23°C,168hr,inEthanol,50%ASTM D471-65 %
Volume change38°C,168hr,inRelativeHumidity,95%ISO 18170.60 %
Change rate of tensile strength in air23°C,168hr,inCascadeDetergentISO 1817-20 %
Quality change rate23°C,168hr,inSodiumHydroxide,50%ASTM D4710.10 %
Volume change23°C,168hr,inEthanol,50%ISO 18176.8 %
Change rate of tensile strength in air38°C,168hr,inRelativeHumidity,90%ISO 1817-16 %
23°C,168hr,inCascadeDetergentASTM D471-20 %
Change rate of ultimate elongation in air23°C,168hr,inSodiumHydroxide,50%ASTM D471-18 %
Volume change in air100°C,168hrASTM D573-1.2 %
Change rate of tensile strength in air23°C,168hr,inSodiumChloride,15%ISO 1817-18 %
Quality change rate23°C,168hr,inClorox,10%ASTM D4710.60 %
Volume change23°C,168hr,inHydrochloricAcid,10%ASTM D4710.40 %
Shore hardnessShoreA,100°C,672hrISO 188-2.0
Change rate of ultimate elongation in air23°C,168hr,inClorox,10%ASTM D471-4.0 %
Quality change rate23°C,168hr,inEthanol,50%ASTM D4716.5 %
Tensile stress change rate23°C,168hr,inCascadeDetergent，BreakISO 1817-7.0 %
Change rate of tensile strength in air23°C,24hr,inIRM903OilASTM D471-4.0 %
Volume change23°C,168hr,inSodiumHydroxide,50%ISO 18170.20 %
Volume change in air100°C,168hrISO 188-1.2 %
Tensile stress change rate23°C,168hr,inEthanol,50%，BreakISO 1817-66 %
23°C,168hr,inClorox,10%，BreakISO 1817-4.0 %
Change rate of tensile strength in air23°C,168hr,inRelativeHumidity,90%ISO 1817-11 %
Hardness change rate in the airShoreA,23°C,168hr,inDeionizedWaterASTM D471-1.0
Volume change23°C,168hr,inSodiumHydroxide,50%ASTM D4710.20 %
Quality change rate23.0°C,168hr,inCascadeDetergentISO 18170.10 %
Volume change23°C,168hr,inHydrochloricAcid,10%ISO 18170.40 %
Quality change rate23°C,168hr,inHydrochloricAcid,10%ASTM D4710.40 %
Volume change23°C,168hr,inEthanol,50%ASTM D4716.8 %
Change rate of tensile strength in air23°C,168hr,inSodiumHydroxide,50%ASTM D471-22 %
Quality change rate23.0°C,168hr,inEthanol,50%ISO 18176.5 %
Change rate of tensile strength in air23°C,168hr,inRelativeHumidity,90%ASTM D471-11 %
Volume change38°C,168hr,inRelativeHumidity,95%ASTM D4710.60 %
Tensile stress change rate23°C,168hr,inHydrochloricAcid,10%，BreakISO 1817-10 %
Volume change23°C,168hr,inClorox,10%ISO 18170.60 %
Quality change rate38.0°C,168hr,inRelativeHumidity,95%ISO 18170.60 %
elastomerTest ConditionTest MethodCELANESE USA/291-60B150
elongationBreak,23°C，Across FlowASTM D412540 %
tensile strengthBreak,23°CISO 378.00 Mpa
Tensile stress100%Strain,23°C，横向FlowASTM D4122.10 Mpa
Permanent compression deformation70°C,22hrISO 81562 %
70°C,22hrASTM D395B62 %
tensile strengthBreak,23°C，横向FlowASTM D4128.00 Mpa
elongationBreak,23°C，Across FlowISO 37540 %
tear strength23°C，横向FlowASTM D62428.0 kN/m
23°C，Across Flow (Across Flow)ISO 34-128 kN/m
Permanent compression deformation23°C,22hrASTM D395B34 %
23°C,22hrISO 81534 %
Tensile stress100%Strain,23°C，横向FlowISO 372.10 Mpa
hardnessTest ConditionTest MethodCELANESE USA/291-60B150
Shore hardnessShoreA,15Sec,23°CISO 86865

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China